本文關(guān)鍵詞：低溫條件下SRⅡ型外加劑對(duì)混凝土力學(xué)與耐久性能的研究　出處：《沈陽(yáng)工業(yè)大學(xué)》2017年碩士論文　論文類型：學(xué)位論文

  更多相關(guān)文章： 混凝土 抗凍耐久性指標(biāo) 無(wú)氯無(wú)堿型防凍劑 XRD 機(jī)理分析

【摘要】：全面探究混凝土抗凍耐久性指標(biāo)的同時(shí),新型無(wú)氯·無(wú)堿型混凝土防凍劑作為一種有效、經(jīng)濟(jì)、環(huán)保的抗凍手段對(duì)水泥基制品作用機(jī)理以及抗凍耐久性能的改善方面也應(yīng)進(jìn)行深入探究。對(duì)不同凍結(jié)條件下的混凝土試件進(jìn)行抗壓強(qiáng)度、孔隙率、透氣性、回彈強(qiáng)度、表面含水率、碳化以及單邊凍融循環(huán)實(shí)驗(yàn)(CIF)后的重量損失、彈性模量損失等試驗(yàn),綜合比較分析后的結(jié)果表明混凝土試件在負(fù)溫下的養(yǎng)護(hù)溫度越低,恢復(fù)標(biāo)準(zhǔn)養(yǎng)護(hù)溫度后強(qiáng)度恢復(fù)越好;混凝土試件特倫托透氣系數(shù)小于10×10~(-16)m~2且回彈強(qiáng)度比大于85%,可以作為混凝土抗凍耐久性指標(biāo)。針對(duì)我國(guó)目前相對(duì)比較空白的新型無(wú)氯·無(wú)堿型混凝土防凍劑,對(duì)摻加不同摻量防凍劑的水泥砂漿試件在不同凍結(jié)、養(yǎng)護(hù)條件下的各項(xiàng)性能、凍融循環(huán)后的抗凍耐久性能展開深入研究;并借助X-Ray物質(zhì)衍射分析對(duì)摻入無(wú)氯無(wú)堿型防凍劑的砂漿試件水化作用機(jī)理進(jìn)行探討。試驗(yàn)結(jié)果表明該種新型無(wú)氯·無(wú)堿型防凍劑對(duì)普通硅酸鹽水泥的最優(yōu)配比為4%;�；郀t礦渣水泥的最優(yōu)配比為5%。新型無(wú)氯無(wú)堿型防凍劑不但可以降低砂漿試件中液相冰點(diǎn),保證砂漿內(nèi)部孔隙組織的完整性,還可以促進(jìn)水泥水化生成物進(jìn)行二次水化,增加水泥基制品強(qiáng)度,顯著改善水泥基抗凍耐久性能。
[Abstract]:At the same time, a new type of non-chlorine and alkali-free concrete antifreeze is an effective and economical one. The mechanism of action and the improvement of anti-freezing durability of cement based products should also be deeply explored. The compressive strength, porosity and permeability of concrete specimens under different freezing conditions should also be studied. Springback strength, surface moisture content, carbonization and one-sided freeze-thaw cycle test after CIF-weight loss, elastic modulus loss and so on. The results of comprehensive comparison and analysis show that the lower the curing temperature of concrete specimen at negative temperature, the better the strength recovery after restoring the standard curing temperature. The permeability coefficient of Trent to concrete specimen is less than 10 脳 10 ~ (-1) -16m ~ (2) and the rebound strength ratio is more than 85%. It can be used as the durability index of concrete. Aiming at the relatively blank new type of non-chlorine and alkaline-free concrete antifreeze agent in our country, the concrete mortar specimens with different amount of antifreeze agent are frozen in different amounts. The properties and durability of freeze-thaw cycle under curing condition are studied deeply. The hydration mechanism of mortar specimens mixed with chlorine-free alkali-free antifreeze was discussed by means of X-Ray material diffraction analysis. The test results show that the new type of non-chlorine and alkali-free antifreeze is the most effective for ordinary Portland cement. The optimum ratio is 4. The optimum ratio of granulated blast furnace slag cement is 5. The new non-chlorine-free alkali-free antifreeze can not only reduce the liquid phase freezing point in mortar specimen, but also ensure the integrity of internal pore structure of mortar. It can also promote the secondary hydration of cement hydration products, increase the strength of cement based products, and significantly improve the durability of cement based freezing resistance.
【學(xué)位授予單位】：沈陽(yáng)工業(yè)大學(xué)
【學(xué)位級(jí)別】：碩士
【學(xué)位授予年份】：2017
【分類號(hào)】：TU528

【參考文獻(xiàn)】

相關(guān)期刊論文 前10條

1 曾春霞;鄧溫悌;;結(jié)構(gòu)混凝土鉆芯法檢驗(yàn)評(píng)定方法探討[J];廣東公路交通;2016年02期

2 劉浪濤;邵式亮;許金余;孫惠香;;混凝土防凍劑的研究進(jìn)展[J];材料導(dǎo)報(bào);2015年13期

3 王曦東;董建忠;王利峰;趙建玲;;防凍劑對(duì)混凝土性能影響的研究現(xiàn)狀[J];公路交通科技(應(yīng)用技術(shù)版);2013年12期

4 吳蓬;呂憲俊;胡術(shù)剛;張磊;;粒化高爐礦渣膠凝性能活化研究進(jìn)展[J];金屬礦山;2012年10期

5 徐洪坤;蔡漢;;摻粉煤灰機(jī)場(chǎng)道面混凝土抗凍融試驗(yàn)研究[J];四川建筑科學(xué)研究;2012年03期

6 吳興;;簡(jiǎn)述礦渣的活性及影響其活性的因素[J];科技風(fēng);2012年08期

7 王超;;復(fù)合防凍劑的防凍機(jī)理及施工要求[J];武漢紡織大學(xué)學(xué)報(bào);2011年06期

8 張雄;魯輝;張永娟;趙明;;礦渣活性激發(fā)方式的研究進(jìn)展[J];西安建筑科技大學(xué)學(xué)報(bào)(自然科學(xué)版);2011年03期

9 張磊;李曉;;BFJ聚羧酸高效減水劑專用防凍劑的研究[J];混凝土;2011年06期

10 宋元蓉;;混凝土防凍劑的原理及使用[J];科技風(fēng);2010年18期

相關(guān)博士學(xué)位論文 前1條

1 商懷帥;引氣混凝土凍融循環(huán)后多軸強(qiáng)度的試驗(yàn)研究[D];大連理工大學(xué);2006年

相關(guān)碩士學(xué)位論文 前4條

1 裴少麗;改性纖維增強(qiáng)聚合物水泥砂漿的制備與性能試驗(yàn)研究[D];長(zhǎng)沙理工大學(xué);2014年

2 尹有君;凍融條件下濕篩大骨料混凝土多軸強(qiáng)度的試驗(yàn)研究[D];大連理工大學(xué);2008年

3 張穎;混凝土材料細(xì)觀結(jié)構(gòu)與抗凍融性的研究[D];蘭州交通大學(xué);2007年

4 張文平;新型混凝土引氣劑和防凍劑研究[D];大連理工大學(xué);2006年

，

本文編號(hào)：1417875