【摘要】：通過7組鋼筋混凝土墩柱的通電銹蝕及干濕循環(huán)試驗,研究氯鹽侵蝕和干濕循環(huán)作用對混凝土墩柱銹脹裂縫形態(tài)及分布的影響。試驗通過控制通電電流和通電時間得到試件不同的鋼筋腐蝕率;通過控制試件浸泡鹽溶液的水位高低的周期性變化實現(xiàn)試件的干濕循環(huán)作用。試驗結(jié)果表明:在腐蝕率相近時,干濕循環(huán)腐蝕試件相較單一腐蝕試件而言,其銹脹裂縫數(shù)量有著明顯的增加,試件的最大裂縫寬度至多增加約100%,其平均裂縫寬度則至多增加約83.3%。
[Abstract]:Through the electrical corrosion and dry and wet cycle tests of 7 groups of reinforced concrete pier columns, The effects of chloride erosion and dry and wet cycling on the form and distribution of rust expansion crack of concrete pier column were studied. The corrosion rate of steel bar was obtained by controlling the current and time of electrification. By controlling the periodic variation of the water level of the salt solution, the dry and wet cycle of the specimen is realized. The test results show that when the corrosion rate is similar, the dry and wet cycle corrosion specimen is better than the single corrosion specimen. The maximum crack width of the specimen increases by about 100 at most, and the average crack width increases by about 83.3 percent at most.
【作者單位】： 上海交通大學船舶海洋與建筑工程學院;
【基金】：國家自然科學基金項目(51178264) 鐵道部科技研究開發(fā)項目(J2011G003)
【分類號】：TV33

【相似文獻】

相關期刊論文 前10條

1 何忠意;鄧安;周亞東;王海波;;干濕循環(huán)下復合固廢填料配比對強度的影響[J];建筑材料學報;2011年06期

2 薛文;王衛(wèi)侖;龔順風;金偉良;;干濕循環(huán)下氯離子在混凝土中的傳輸[J];低溫建筑技術;2010年06期

3 曹光栩;宋二祥;徐明;;碎石料干濕循環(huán)變形試驗及計算方法[J];哈爾濱工業(yè)大學學報;2011年10期

4 袁璞;馬芹永;;干濕循環(huán)條件下煤礦砂巖分離式霍普金森壓桿試驗研究[J];巖土力學;2013年09期

5 李克鋼;吳勇;鄭東普;;砂巖力學特性對干濕循環(huán)效應響應規(guī)律的試驗研究[J];北京理工大學學報;2013年10期

6 張俊然;許強;孫德安;;多次干濕循環(huán)后土-水特征曲線的模擬[J];巖土力學;2014年03期

7 張偉勤;劉連新;代大虎;;混凝土在鹵水、淡水中的干濕循環(huán)腐蝕試驗研究[J];青海大學學報(自然科學版);2006年04期

8 李克鋼;鄭東普;黃維輝;;干濕循環(huán)作用下砂巖力學特性及其本構模型的神經(jīng)網(wǎng)絡模擬[J];巖土力學;2013年S2期

9 劉文化;楊慶;唐小微;李吳剛;;干濕循環(huán)條件下不同初始干密度土體的力學特性[J];水利學報;2014年03期

10 李固華;高波;;納米CaCO_3對砼耐干濕循環(huán)腐蝕性能的影響[J];重慶交通學院學報;2007年02期

相關會議論文 前6條

1 衛(wèi)軍;余t，

本文編號：1624572