本文選題：剎車片 + 激光熔覆　； 參考：《熱加工工藝》2016年14期

【摘要】：采用激光熔覆方法在Q235鋼基體表面制備一種高強(qiáng)度、高硬度和高耐磨性的涂層。同時(shí)借助光學(xué)顯微鏡、洛氏硬度計(jì)和磨粒磨損試驗(yàn)機(jī)等手段,研究超聲波功率對(duì)涂層組織與性能的影響。結(jié)果表明:超聲波功率對(duì)涂層組織與性能影響顯著。隨超聲波功率的增大,在空化效應(yīng)以及聲流作用下,涂層顯微組織逐漸細(xì)化。涂層硬度與相對(duì)耐磨性都呈先增加后減小的變化規(guī)律。當(dāng)超聲波功率增大到1000 W時(shí),涂層組織非常細(xì)小,硬度達(dá)到最大值62 HRC,相對(duì)耐磨性達(dá)到最大值,其耐磨性是基體的24倍左右。
[Abstract]:A kind of coating with high strength, high hardness and high wear resistance was prepared on Q235 steel substrate by laser cladding. The influence of ultrasonic power on the microstructure and properties of the coating was studied by means of optical microscope, Rockwell hardness tester and abrasive wear tester. The results show that ultrasonic power has a significant effect on the microstructure and properties of the coating. With the increase of ultrasonic power, the microstructure of the coating is gradually refined under the effect of cavitation and acoustic flow. The hardness and relative wear resistance of the coating increased first and then decreased. When the ultrasonic power is increased to 1000 W, the microstructure of the coating is very fine, the hardness reaches the maximum value of 62 HRC, the relative wear resistance reaches the maximum, and the wear resistance of the coating is about 24 times that of the substrate.
【作者單位】： 湖南汽車工程職業(yè)學(xué)院;江西昌河鈴木汽車有限公司;
【分類號(hào)】：U463.5;TG174.4

【相似文獻(xiàn)】

相關(guān)期刊論文 前6條

1 李軍文;桃野正;付瑩;;超聲波功率對(duì)鑄錠內(nèi)的氣孔及組織細(xì)化的影響[J];鑄造;2007年02期

2 李軍文;郭文濤;韓志凡;顏宏;;超聲波功率對(duì)ZA27合金凝固組織及力學(xué)性能的影響[J];熱加工工藝;2011年13期

3 林莉,李喜孟,譚家隆,張俊善;超聲波功率譜技術(shù)無(wú)損區(qū)分GCr15SiMn鋼顯微組織的探討[J];金屬熱處理學(xué)報(bào);2002年04期

4 李杰;陳偉慶;王曉峰;;超聲波功率對(duì)高碳鋼中夾雜物的影響[J];北京科技大學(xué)學(xué)報(bào);2009年09期

5 李杰;陳偉慶;;超聲波熔體處理對(duì)高碳鋼凝固組織和性能的影響[J];鑄造;2008年10期

6 ;[J];;年期

相關(guān)會(huì)議論文 前1條

1 郭文濤;李軍文;賈征;;超聲波功率對(duì)ZA27合金凝固組織及力學(xué)性能的影響[A];2009中國(guó)鑄造活動(dòng)周論文集[C];2009年

，

本文編號(hào)：1901021