本文選題：尾礦 + 細砂　； 參考：《遼寧科技大學》2017年碩士論文

【摘要】：尾礦壩作為一種特殊的水工建筑物,與普通的擋水壩有很大區(qū)別,尾礦壩的安全穩(wěn)定對礦山生產、周圍生態(tài)環(huán)境以及附近居民的生命財產安全至關重要。應用SLB-1型應力應變控制式三軸剪切滲透試驗儀,對大孤山尾礦庫的尾礦細砂進行了三軸壓縮試驗研究,分析研究了尾礦細砂在不同應力路徑和固結度下的變形破壞特性。(1)通過尾礦砂的篩分實驗以及K0固結試驗,確定尾礦砂試樣屬于細砂,尾礦砂的靜止側壓力系數為0.23。(2)通過對尾礦細砂在3種不同主應力比下的固結不排水試驗,以及對應力應變曲線的分析,獲得了主應力比對尾礦細砂變形特性的影響。隨著主應力比的不同,尾礦細砂抵抗變形的能力有很大區(qū)別,在主應力比較小時,試樣本身容易發(fā)生變形突變,產生破壞。在主應力比較大時,軸向力即使增加到很大,試樣的軸向變形量依然很小;主應力比不同時,即使軸壓相同,由于圍壓不同,試樣所反映的抗剪強度有很大區(qū)別。(3)尾礦細砂由于堆積時間、空間的不同和排水條件各異,在尾礦庫中的固結程度也大不相同。為研究尾礦細砂在不同固結度下的力學性質,進行了多種固結度下的固結不排水試驗。試驗結果表明當固結度不同時,主應力差的峰值變化幅度并不隨著固結度單調增加,在圍壓100kPa下主應力差的峰值變化幅度可從356.8kPa到479.5kPa;粘聚力隨著固結度的增加逐漸減小,內摩擦角變化幅度比較小。
[Abstract]:As a special hydraulic structure, tailings dam is very different from common dam. The safety and stability of tailings dam is very important to mine production, the surrounding ecological environment and the life and property safety of nearby residents.The triaxial compression test of fine tailing sand in Dagushan tailings reservoir was carried out by using SLB-1 type stress and strain control triaxial shear permeation tester.The deformation and failure characteristics of tailing fine sand under different stress paths and consolidation degrees are analyzed and studied. Through the screening experiment of tailings sand and the K0 consolidation test, it is determined that the tailings sand samples belong to fine sand.The static lateral pressure coefficient of tailings is 0.23.m2) the influence of principal stress ratio on the deformation characteristics of fine tailing sand is obtained through the consolidation undrained test of tailings fine sand under three different principal stress ratios and the analysis of stress-strain curve.With the difference of principal stress ratio, the ability of fine tailing sand to resist deformation is very different. When the principal stress ratio is small, the specimen itself is prone to deformation, mutation and failure.When the principal stress is relatively large, the axial deformation of the specimen is still very small even if the axial force is increased to a large extent, and when the principal stress ratio is different, even if the axial pressure is the same, because of the different confining pressure,The shear strength reflected by the specimen is very different. (3) due to the different accumulation time, different space and different drainage conditions, the consolidation degree of the tailings fine sand in the tailings reservoir is also very different.In order to study the mechanical properties of tailing fine sand under different consolidation degrees, undrained consolidation tests were carried out under various consolidation degrees.The experimental results show that the range of peak variation of principal stress difference does not increase monotonously with consolidation when consolidation degree is different, the peak value of principal stress difference can range from 356.8kPa to 479.5 KPA under confining pressure 100kPa, and the cohesive force decreases gradually with the increase of consolidation degree.The variation of the angle of internal friction is relatively small.
【學位授予單位】：遼寧科技大學
【學位級別】：碩士
【學位授予年份】：2017
【分類號】：TD926.4

【參考文獻】

相關期刊論文 前10條

1 王慶滿;;尾礦壩壩料的動力特性研究[J];地下水;2015年03期

2 汪洪星;楊春和;陳鋒;冒海軍;;軟土抗剪強度指標隨固結度變化規(guī)律分析[J];巖土力學;2014年S1期

3 鄧金迪;;榆木溝尾礦庫排滲技術探討[J];現代礦業(yè);2014年01期

4 穆連萍;王譽聞;孟繁斌;蘇芳莉;;本溪市南芬選礦廠尾礦庫生態(tài)恢復治理實踐[J];中國水土保持;2013年07期

5 劉海明;楊春和;張超;冒海軍;曹凈;;高壓下尾礦材料冪函數型摩爾強度特性研究[J];巖土力學;2012年07期

6 彭芳樂;白小宇;雷亮;;多種應力路徑條件下上海粉細砂的室內試驗[J];同濟大學學報(自然科學版);2011年12期

7 馬獻民;于丹;周志廣;;鞍鋼礦業(yè)公司大孤山尾礦壩滲流場數值分析[J];山西建筑;2011年05期

8 譚欽文;李軍林;徐濤;;中線法堆壩尾礦料的動力特性實驗研究[J];自然災害學報;2010年04期

9 許成順;文利明;杜修力;徐海濱;;不同應力路徑條件下的砂土剪切特性試驗研究[J];水利學報;2010年01期

10 唐炫;魏麗敏;胡海軍;;不同固結度下軟土的力學特性[J];鐵道勘察;2009年04期

相關博士學位論文 前1條

1 潘建平;尾礦壩抗震設計方法及抗震措施研究[D];大連理工大學;2007年

相關碩士學位論文 前5條

1 王宇鴿;高應力飽和尾砂剪切強度特性研究[D];江西理工大學;2015年

2 崔彥平;連續(xù)加卸載條件下重塑黃土K_0固結特性研究[D];長安大學;2014年

3 劉湘平;飽和尾礦穩(wěn)態(tài)特性試驗研究[D];江西理工大學;2014年

4 張楊;尾礦壩抗滑穩(wěn)定可靠度分析[D];長沙理工大學;2010年

5 張一軍;細粒土尾礦壩穩(wěn)定性研究[D];長安大學;2007年

，

本文編號：1731477