【摘要】：為提高石蠟作為相變蓄冷材料的導(dǎo)熱性能,制備了碳納米管添加量分別為0%、1%、2%、3%、4%、5%的石蠟-碳納米管復(fù)合材料,并對其熱物性及穩(wěn)定性進(jìn)行實驗研究。結(jié)果表明,隨著碳納米管添加量的增加,復(fù)合材料的相變溫度基本不變,相變潛熱逐漸減小,導(dǎo)熱系數(shù)逐漸增大。在添加量為5%時,復(fù)合材料的融化和凝固相變潛熱分別為128.2 J/g和134.4 J/g,比純石蠟相對減小了15.5%和13.8%;固態(tài)和液態(tài)導(dǎo)熱系數(shù)分別為0.487 W/(m·K)和0.516 W/(m·K),比純石蠟相對提高了39.5%和40.3%,同時具有較好的循環(huán)穩(wěn)定性。
[Abstract]:In order to improve the thermal conductivity of paraffin as a phase change material, a paraffin-carbon nanotube composite containing 0% carbon nanotube (CNT) was prepared. The thermal properties and stability were studied experimentally. The results show that with the increase of the content of carbon nanotubes, the phase transition temperature of the composites is basically unchanged, the latent heat of phase transition decreases gradually, and the thermal conductivity increases gradually. The latent heat of melting and solidification phase transition is 128.2 J / g and 134.4 J / g respectively, which is 15.5% and 13.8% lower than that of pure paraffin. The thermal conductivity of solid and liquid phase is 0.487 W / (m K) and 0.516 W / (m K), respectively, which is 39.5% and 40.3% higher than that of pure paraffin, and has good cycle stability.
【作者單位】： 鄭州輕工業(yè)學(xué)院能源與動力工程學(xué)院;
【基金】：國家自然科學(xué)基金資助項目(No.51476149) 河南省杰出青年基金項目(No.154100510014) 河南省教育廳創(chuàng)新才團(tuán)隊項目(No.17IRTSTHN029)
【分類號】：TB332;TK02

【相似文獻(xiàn)】

相關(guān)期刊論文 前4條

1 駱蘇華,李亞東;Ti_(50)Ni_(40)Cu_(10)合金的相變潛熱及相變熱滯[J];材料科學(xué)與工程學(xué)報;2003年01期

2 滿亞輝;吳文健;;Na_2SO_4·10H_2O相變過程及其相變潛熱的計算[J];國防科技大學(xué)學(xué)報;2009年02期

3 張正國,黃弋峰,方曉明,邵剛;硬脂酸/二氧化硅復(fù)合相變儲熱材料制備及性能研究[J];化學(xué)工程;2005年04期

4 ;[J];;年期

相關(guān)會議論文 前1條

1 張秀榮;汪南;高進(jìn)偉;吳淑英;巨小平;朱冬生;;復(fù)合相變儲熱材料的制備與熱性能研究[A];第七屆中國功能材料及其應(yīng)用學(xué)術(shù)會議論文集（第4分冊）[C];2010年

相關(guān)博士學(xué)位論文 前1條

1 滿亞輝;相變潛熱機(jī)理及其應(yīng)用技術(shù)研究[D];國防科學(xué)技術(shù)大學(xué);2010年

相關(guān)碩士學(xué)位論文 前1條

1 張晗;三元硝酸鹽的改性研究[D];武漢理工大學(xué);2014年

，

本文編號：2296049