本文關(guān)鍵詞：CdSZnO核殼納米棒陣列結(jié)構(gòu)的制備及在太陽能電池中的應(yīng)用　出處：《化工新型材料》2016年03期 　論文類型：期刊論文

  更多相關(guān)文章： ZnO納米棒陣列 電沉積法 CdS納米晶 太陽能電池

【摘要】：采用水熱法制備垂直于FTO導(dǎo)電玻璃基底的ZnO納米棒陣列,然后通過電化學(xué)沉積法在ZnO納米棒陣列上沉積CdS納米晶,形成CdS/ZnO核殼納米棒陣列結(jié)構(gòu)。利用掃描電子顯微鏡(SEM)、X射線衍射儀(XRD)、X射線能譜儀(EDS)和紫外-可見分光光度計(UV-Vis)等對所得樣品的形貌、結(jié)構(gòu)組成進行分析表征;并以其為光電極組裝太陽能電池,研究CdS納米晶厚度對該電池光電性能的影響。結(jié)果表明,所得樣品不僅拓寬和加強電池的光吸收能力,也有效調(diào)控光生載流子的傳輸。當(dāng)CdS納米晶沉積時間為60s時,電池的光電轉(zhuǎn)換效率最高可達1.10%。
[Abstract]:ZnO nanorods arrays perpendicular to FTO conductive glass substrates were prepared by hydrothermal method. Then CdS nanocrystals were deposited on ZnO nanorods by electrochemical deposition. The structure of CdS/ZnO core shell nanorod array was formed. The morphology and structure of the samples were characterized by X-ray energy spectrometer (EDS) and UV-Vis-UV spectrophotometer. The effect of the thickness of CdS nanocrystalline on the photovoltaic performance of the solar cell was studied. The results showed that the sample not only broadens and strengthens the photoabsorption ability of the cell. When the deposition time of CdS nanocrystalline is 60 s, the photovoltaic conversion efficiency can reach 1.10%.
【作者單位】： 遼寧工程技術(shù)大學(xué)理學(xué)院;礦山熱動力災(zāi)害與防治教育部重點實驗室遼寧工程技術(shù)大學(xué)安全科學(xué)與工程學(xué)院;
【基金】：國家科技支撐計劃(2013BAK06B07) 遼寧省教育廳科學(xué)研究項目(L2013138)
【分類號】：TB383.1;TM914.4
【正文快照】： 量子點敏化太陽能電池作為第三代太陽能電池,具有生產(chǎn)成本低廉、工藝簡單及穩(wěn)定性好等優(yōu)點,是近年來的研究熱點之一。ZnO作為一種優(yōu)異的無機半導(dǎo)體材料,成為太陽能電池研究較多的材料,但其禁帶寬度約為3.2eV,僅吸收紫外光,這限制其對可見光的利用[1]。為進一步提高ZnO的光電性，

本文編號：1385399