本文選題：超早期混凝土　切入點(diǎn)：模板　出處：《同濟(jì)大學(xué)學(xué)報(bào)(自然科學(xué)版)》2016年11期 　論文類型：期刊論文

【摘要】：超早期混凝土對(duì)模板的側(cè)向壓力直接影響到模板設(shè)計(jì),其大小受澆筑速度、混凝土配比、溫度、模板表面性態(tài)、尺寸、形狀、澆筑深度等諸多因素影響,作用機(jī)制非常復(fù)雜.在理論分析的基礎(chǔ)上,設(shè)計(jì)了一個(gè)可以測(cè)量不同配比下混凝土對(duì)模板側(cè)向壓力的模型試驗(yàn),并對(duì)試驗(yàn)結(jié)果進(jìn)行了分析.試驗(yàn)結(jié)果表明,側(cè)向壓力豎向分布與靜水壓力相似,但明顯小于靜水壓力;混凝土水灰比(質(zhì)量比)越大,模板初始側(cè)向壓力越接近靜水壓力,側(cè)向壓力下降速度越快;超早期混凝土側(cè)向壓力的消散發(fā)生在潛伏期之后的水化反應(yīng)階段,此階段水化產(chǎn)物的加速形成使材料具有自承載能力,因此側(cè)向壓力迅速下降并最終消失.
[Abstract]:The lateral pressure of super early concrete directly affects the design of the formwork, and its size is affected by many factors, such as pouring speed, concrete ratio, temperature, surface state, size, shape, pouring depth, etc. The mechanism of action is very complicated. On the basis of theoretical analysis, a model test is designed to measure the lateral pressure of concrete to formwork under different proportions, and the experimental results are analyzed. The vertical distribution of lateral pressure is similar to that of hydrostatic pressure, but obviously smaller than that of hydrostatic pressure, the larger the mass ratio of concrete water to cement, the closer the initial lateral pressure of the formwork is to the hydrostatic pressure, and the faster the decrease of lateral pressure is. The dissipation of lateral pressure of super-early concrete occurs in the hydration reaction stage after the incubation period, in which the accelerated formation of hydration products makes the material have self-loading capacity, so the lateral pressure decreases rapidly and finally disappears.
【作者單位】： 天津大學(xué)水利工程仿真與安全國家重點(diǎn)實(shí)驗(yàn)室;中水北方勘測(cè)設(shè)計(jì)研究有限責(zé)任公司;
【基金】：國家自然科學(xué)基金(51321065,51279126) 天津市自然科學(xué)基金(13JCQNJC06800)
【分類號(hào)】：TU755.2

【相似文獻(xiàn)】

相關(guān)期刊論文 前9條

1 王曉峰,趙志縉;滑模施工中早期混凝土受荷的試驗(yàn)研究[J];施工技術(shù)(建筑技術(shù)通訊);1990年05期

2 陳明;盧文波;;超早期混凝土爆破安全振動(dòng)速度的討論[J];工程爆破;2006年02期

3 金賢玉,錢春,錢在茲;對(duì)早期混凝土產(chǎn)生損傷的試驗(yàn)研究與分析[J];土木工程學(xué)報(bào);1997年06期

4 謝成新;鄭建嵐;;早期混凝土軸心受拉試件的制作[J];黑龍江科技學(xué)院學(xué)報(bào);2007年05期

5 崔n，

本文編號(hào)：1640152