【摘要】：通過自由基聚合方法合成聚丙烯酰胺(PAAM)水凝膠、丙烯酰胺(AAM)與甲基丙烯酸(MAA)的不同摩爾比的P(AAM-co-MAA)水凝膠,并對這些水凝膠的形貌和膨脹性能及pH敏感性能進行研究。結(jié)果表明,相比PAAM水凝膠,P(AAM-co-MAA)水凝膠的膨脹性能提高,但當AAM與MAA摩爾比為13∶2時,P(AAM-co-MAA)水凝膠具有更好的膨脹性和pH敏感性。這些水凝膠的特殊性能使它們有望應用于藥物的緩控釋放方面。
[Abstract]:Polyacrylamide (PAAM) hydrogels and P (AAM-co-MAA) hydrogels with different molar ratios of acrylamide (AAM) and (MAA) methacrylate were synthesized by free radical polymerization. The morphology, swelling properties and pH sensitivity of these hydrogels were studied. The results showed that the swelling property of P (AAM-co-MAA) hydrogel was higher than that of PAAM hydrogel, but when the molar ratio of AAM to MAA was 13:2, the swelling property and pH sensitivity of AAM (AAM-co-MAA) hydrogel were better. The special properties of these hydrogels make them promising for slow release of drugs.
【作者單位】： 渭南師范學院化學與生命科學學院;
【基金】：國家自然科學基金項目(51172136) 陜西省教育廳科學研究項目(11JK0579) 軍民融合發(fā)展基金項目(13JMR20)
【分類號】：R318.08

【相似文獻】

相關期刊論文 前7條

1 董宏偉;石四箴;陳克恭;小園凱夫;;快速加熱型石膏包埋料對鑄造精度影響的研究[J];口腔醫(yī)學;2007年04期

2 巢永烈,鄺先昊,廖運茂,王航;鈦合金粉漿涂塑底層冠用耐火代型材料的膨脹性能測試[J];華西口腔醫(yī)學雜志;1999年01期

3 陳鵬;林建華;李柱來;李貴雙;葉曉;;聚甲基丙烯酸-2-羥乙酯水凝膠載藥(類軟骨)膜的制備及性能[J];中國組織工程研究與臨床康復;2009年12期

4 范德增!100083,莫宣學!100081,翁潤生!100081,秦飛!100081;磷酸鹽包埋材料研究[J];北京口腔醫(yī)學;2000年01期

5 李凌冰,譚業(yè)邦,孟建文;丙烯酰胺與葡萄糖烯丙基酰胺共聚水凝膠的合成與釋藥性能研究[J];生物醫(yī)學工程學雜志;2004年06期

6 于煒婷;劉袖洞;李曉霞;綦文濤;任東文;馬小軍;;殼聚糖溶液pH對載細胞海藻酸鈉-殼聚糖微膠囊性能的影響[J];高等學校化學學報;2006年01期

7 劉東陽;彭玉平;曾浩;;經(jīng)蝶顱底重建材料的實驗研究[J];中國醫(yī)學物理學雜志;2011年02期

相關會議論文 前1條

1 李志宏;武繼民;汪鵬飛;黃姝杰;關靜;郭春;郭勇;李瑞欣;張西正;;高膨脹止血海綿的制備及性能研究[A];天津市生物醫(yī)學工程學會第29屆學術(shù)年會暨首屆生物醫(yī)學工程前沿科學研討會論文集[C];2009年

相關博士學位論文 前2條

1 王偉強;冠狀動脈支架力學行為有限元分析及其結(jié)構(gòu)優(yōu)化[D];大連理工大學;2006年

2 李寧;冠狀動脈支架力學性能數(shù)值研究與優(yōu)化設計[D];大連理工大學;2011年

相關碩士學位論文 前1條

1 斯清慶;明膠—幾丁糖交聯(lián)膜的制備及防粘連功能的實驗研究[D];第二軍醫(yī)大學;2003年

，

本文編號：2201257