本文選題：血管支架 + 無鎳��； 參考：《稀有金屬材料與工程》2014年S1期

【摘要】：目前臨床上使用鈷鉻鎢鎳合金(L605)的高強(qiáng)度特性保證支架網(wǎng)絲直徑較傳統(tǒng)支架降低30%左右,平均直徑在80μm左右,有效減小了支架對(duì)內(nèi)膜組織的刺激,減少了支架再狹窄的潛在誘因,臨床療效明顯。但是L605合金和傳統(tǒng)的316L不銹鋼一樣,其中含有10%左右的鎳元素。大量臨床研究表明,鎳有致敏、致癌和誘發(fā)血栓等毒副作用,而且鎳離子對(duì)血管內(nèi)膜的過敏刺激反應(yīng)以及其與再狹窄的相互關(guān)系一直存在爭議。針對(duì)傳統(tǒng)醫(yī)用鈷基合金中潛在的鎳離子危害,研究開發(fā)了一種新型血管支架用無鎳鈷基合金Co-20Cr-12Fe-18Mn-2Mo-4W-N,通過補(bǔ)充人體必需微量元素鐵Fe和錳Mn元素來替代部分昂貴鈷元素。和傳統(tǒng)的L605合金相比,新型無鎳鈷基合金的抗拉強(qiáng)度達(dá)到1000 MPa以上,延伸率達(dá)到55%以上。同時(shí)新型無鎳鈷基合金具有優(yōu)良的耐蝕性能,點(diǎn)蝕電位高達(dá)1000 mV以上。新型無鎳鈷基合金優(yōu)良的強(qiáng)韌性和耐蝕性,有望成為新一代血管支架材料。
[Abstract]:At present, the high strength characteristic of Cobalt-Cr-W-Ni alloy (L605) ensures that the diameter of the mesh wire decreases by about 30% and the average diameter is about 80 渭 m compared with the traditional stent, which effectively reduces the stimulation of the stent to the endometrial tissue. The potential inducement of stent restenosis is reduced, and the clinical effect is obvious. But the L605 alloy, like the conventional 316L stainless steel, contains about 10% nickel. A large number of clinical studies have shown that nickel has toxic side effects, such as sensitization, carcinogenesis and thrombosis, and the allergic response of nickel ion to vascular intima and its relationship with restenosis have been controversial. In view of the potential nickel ion hazards in traditional medical cobalt-based alloys, a new nickel-free cobalt-based alloy Co-20Cr-12Fe-18Mn-2Mo-4W-N for vascular stents was developed. Some expensive cobalt elements were replaced by supplementation of the necessary trace elements Fe Fe and mn to replace some expensive cobalt elements. Compared with the traditional L605 alloy, the tensile strength and elongation of the new Nickel-Cobalt base alloy are over 1000 MPa and 55%, respectively. At the same time, the new nickel-free cobalt-base alloy has excellent corrosion resistance, the pitting potential is over 1000 MV. New nickel-free cobalt-based alloys are expected to be a new generation of vascular scaffolds due to their excellent strength and corrosion resistance.
【作者單位】： 中國科學(xué)院金屬研究所;
【基金】：國家自然科學(xué)基金(31370976) 國家重點(diǎn)基礎(chǔ)研究發(fā)展計(jì)劃“973”(2012CB619101)
【分類號(hào)】：R318.08

【共引文獻(xiàn)】

相關(guān)期刊論文 前1條

1 ZHANG Bin;CHEN Ming;ZHENG Bo;WANG Xin Gang;WANG Xi Ting;FAN Yuan Yuan;HUO Yong;;A Novel High Nitrogen Nickel-free Coronary Stents System: Evaluation in a Porcine Model[J];Biomedical and Environmental Sciences;2014年04期

【相似文獻(xiàn)】

相關(guān)會(huì)議論文 前3條

1 王銘;張東惠;;醫(yī)用介入器械鈦合金導(dǎo)絲的開發(fā)與應(yīng)用(綜述)[A];天津市生物醫(yī)學(xué)工程學(xué)會(huì)第30次學(xué)術(shù)年會(huì)暨生物醫(yī)學(xué)工程前沿科學(xué)研討會(huì)論文集[C];2010年

2 楊曉華;任先京;;Ce對(duì)低氧含量鈷基合金粉末的制備及其性能的影響[A];2009全國粉末冶金學(xué)術(shù)會(huì)議論文集[C];2009年

3 楊忠波;楊勇飛;;鈷基合金焊絲及其制備工藝[A];四川省機(jī)械工程學(xué)會(huì)粉末冶金專委會(huì)學(xué)術(shù)交流會(huì)、成都市2007科技年機(jī)械工程學(xué)會(huì)粉冶年會(huì)論文集[C];2007年

相關(guān)碩士學(xué)位論文 前6條

1 洪亮亮;添加劑對(duì)電沉積鈷基合金的結(jié)構(gòu)及性能的影響研究[D];華僑大學(xué);2007年

2 趙君威;微波消解/ICP-AES法測(cè)定鈷基合金中多元素的方法研究[D];機(jī)械科學(xué)研究總院;2013年

3 鄭婷;TC4鈦合金表面鈷基合金層的制備及性能研究[D];南京航空航天大學(xué);2010年

4 史勝鳳;醫(yī)用鈷基合金的組織結(jié)構(gòu)及耐腐蝕性能[D];浙江大學(xué);2006年

5 謝豐豪;微波燒結(jié)制備陶瓷表面鈷基合金功能涂層的研究[D];河南科技大學(xué);2014年

6 楊承鳳;鈷基合金用高效緩蝕清洗劑及其性能研究[D];機(jī)械科學(xué)研究總院;2012年

，

本文編號(hào)：1872810