文獻名稱：PVC與核殼結構聚丙烯酸酯及環(huán)氧樹脂的共混增韌

    前言：研究發(fā)現(xiàn)由分段乳液聚合丙烯酸丁酯、甲基丙烯酸甲酯、甲基丙烯酸縮水甘油酯制備的三層核殼結構共聚體和少量環(huán)氧樹脂(含固化劑及促進劑)與PVC在適當配比下共混,可使改性PVC的抗沖擊性能明顯提高�？疾炝斯不祗w系的組成與其沖擊強度及斷裂形態(tài)之間的關系。
    Core-shell particles for toughening PVC were prepared by sequential emulsion polymerization of butyl acrylate(BA) , methyl methacrylate(MMA) and glycidyl methacrylate (GMA). Blending of these particles and small amounts of epoxy resin, including curing agent and accelerator, together with PVC gives materials with greatly enhanced impact strength at a optimized weight fraction. Dependence of impact strength and fracture morphology of the toughened PVC material upon the variation of blending composition has b...

文獻名稱 PVC與核殼結構聚丙烯酸酯及環(huán)氧樹脂的共混增韌

Article Name
英文(英語)翻譯 Toughening of PVC via Blending of Core-Shell Polyacrylic-ester Copolymer and Epoxy Resin;

作者 張保龍; 王淑芳; 黃吉甫; 丁培元; 杜宗杰; 宋謀道; 張邦華;

Author ZHANG Bao-Long;WANG Shu-Fang;HUANG Ji-Fu;DING Pel-Yuan;DU Zhong-Jie （Departntent of Chemistry;Nankai University;Tianjin;300071）SONG Mou-Dao;ZHANG Bang-Hua （Institute of Polymer Chemistry;300071）;

作者單位
Author Agencies 南開大學化學系; 南開大學高分子化學研究所; 南開大學高分子化學研究所 天津;

文獻出處
Article From 中國科學院上海冶金研究所; 材料物理與化學(專業(yè)) 博士論文 2000年度

關鍵詞 核殼結構共聚體; 環(huán)氧樹脂; PVC; 甲基丙烯酸縮水甘油酯;

Keywords Core-shell copolymer;Epoxy resin;PVC;Glycidyl methacrylate;

新型絡合吸附劑的研究(Ⅱ)——銅離子模板高分子多乙烯多胺絡合吸附劑的合成和特性
乳液聚合共聚物玻璃化轉(zhuǎn)變溫度及其理論計算
TiCl_4/Al_2Et_3Cl_3/Y-型分子篩高效乙烯丙烯共聚催化體系的研究
α-烴基取代吡啶對金(Ⅲ)的萃取研究(Ⅰ)——電離常數(shù)的測定和金的萃取行為
MZr_2(AsO_4)_3(M=Na,K,Rb,Cs)的水熱合成與結構表征
α-和β-[SiW_9O_(37)M_3(H_2O)_3]~(7-)(M=A1~(3+),Ga~(3+),In~(3+))的合成和鎢-183核磁共振研究
鐵-磷-硼納米金屬玻璃的化學制備與穆斯堡爾研究
α-烴基取代吡啶對金(Ⅲ)的萃取研究(Ⅱ)
差示脈沖極譜法對鎘(Ⅱ)-草酸-琥珀酸混配三元配合物的研究
非配對型電極上的示波沉淀滴定

  本文關鍵詞：張保龍，，由筆耕文化傳播整理發(fā)布。