本文選題：油罐　切入點(diǎn)：石墨烯　出處：《表面技術(shù)》2017年11期 　論文類型：期刊論文

【摘要】：目的探究石墨烯基防護(hù)涂層/碳鋼體系在原油儲罐沉積水中的防護(hù)機(jī)制。方法以實(shí)際原油儲罐的沉積水為腐蝕介質(zhì),以自制石墨烯底漆和石墨烯面漆為防護(hù)涂層體系,采用交流阻抗譜、動電位極化曲線,結(jié)合鹽霧實(shí)驗(yàn)探究石墨烯涂層體系在沉積水中的腐蝕行為和失效衍化機(jī)制。結(jié)果石墨烯底漆在浸泡初期對碳鋼具有一定的防護(hù)效果,隨著浸泡時(shí)間的延長,水分子逐漸滲透涂層,涂層逐漸失效。采用石墨烯面漆和石墨烯底漆搭配,可顯著提高涂層對碳鋼在沉積水中的防護(hù)性能,浸泡46 d后,涂層電阻仍為162 M?·cm。結(jié)論石墨烯底漆和石墨烯面漆涂層體系對儲罐底板在沉積水中具有良好的防護(hù)性能,研究成果對油罐底板涂層防護(hù)選材具有理論指導(dǎo)意義。
[Abstract]:Objective to explore the protective mechanism of graphene based protective coating / carbon steel system in the water deposited from crude oil tank. Methods the corrosion medium of the actual crude oil tank was used as corrosion medium, and the self-made graphene primer and graphene topcoat were used as protective coating system. The corrosion behavior and failure evolution mechanism of graphene coating system in deposited water were investigated by means of AC impedance spectroscopy, potentiodynamic polarization curve and salt spray test. Results the graphene primer had a certain protective effect on carbon steel in the early stage of soaking. With the prolongation of soaking time, the water molecules gradually permeate the coating, and the coating gradually fails. The protective performance of the coating on carbon steel in the deposited water can be improved significantly by using the combination of graphene topcoat and graphene primer, and the coating is soaked for 46 days. The coating resistance is still 162m? Conclusion the coating system of graphene primer and graphene topcoat has good protective performance on tank bottom in the depositional water, and the research results are of theoretical significance for the selection of coating materials for oil tank bottom plate.
【作者單位】： 浙江海洋大學(xué)船舶與機(jī)電工程學(xué)院;中國科學(xué)院寧波材料技術(shù)與工程研究所中國科學(xué)院海洋新材料與應(yīng)用技術(shù)重點(diǎn)實(shí)驗(yàn)室浙江省海洋材料與防護(hù)技術(shù)重點(diǎn)實(shí)驗(yàn)室;蕪湖春風(fēng)新材料有限公司;
【基金】：國家自然科學(xué)基金(41506098) 中國博士后基金和第九批特等資助項(xiàng)目(2015M580528,2016T90553) 浙江省博士后科研項(xiàng)目擇優(yōu)資助項(xiàng)目(BSH1502160) 寧波市自然科學(xué)基金(2016A610261)~~
【分類號】：TE988

【相似文獻(xiàn)】

相關(guān)期刊論文 前5條

1 劉玲莉;;原油儲罐沉積水對罐底板的腐蝕分析[J];油田地面工程;1993年06期

2 鄔康迪;曾為民;汪文強(qiáng);馬玉錄;;原油儲罐沉積水腐蝕的靜態(tài)掛片實(shí)驗(yàn)研究[J];化工裝備技術(shù);2013年06期

3 汪文強(qiáng);曾為民;馬玉錄;;碳鋼在原油儲罐沉積水中的電化學(xué)行為[J];腐蝕與防護(hù);2014年04期

4 賈思洋;李超;韓東銳;;B610E不同焊接接頭在石油沉積水中的耐蝕性研究[J];裝備環(huán)境工程;2012年06期

5 李超;賈思洋;張波;;儲罐鋼08MnNiVR和SPV490Q在石油沉積水中腐蝕性能對比[J];裝備環(huán)境工程;2013年05期

相關(guān)博士學(xué)位論文 前1條

1 雷廣平;H_2S/CH_4及CO_2/CH_4混合物分離的分子模擬研究[D];重慶大學(xué);2015年

相關(guān)碩士學(xué)位論文 前1條

1 李偉;氧化石墨烯及其納米復(fù)合物在油介質(zhì)中的摩擦學(xué)研究[D];揚(yáng)州大學(xué);2017年

，

本文編號：1588734