本文選題：自密實混凝土 + 橡膠顆粒　； 參考：《硅酸鹽學報》2014年08期

【摘要】：研究了以橡膠顆粒等體積取代細骨料時,不同橡膠顆粒取代量對自密實混凝土的工作性、抗壓強度、應力--應變曲線、抗凍性能、抗硫酸鹽干濕循環(huán)性能以及電通量等性能的影響。結果表明:橡膠顆粒對新拌自密實混凝土工作性和硬化自密實混凝土性能均有較大影響;橡膠顆粒取代量在15%(體積分數,下同)以內時,橡膠顆粒的摻入可較好地改善新拌自密實混凝土工作性;橡膠顆�？娠@著提高自密實混凝土的峰值應變以及抗離子滲透性能,橡膠顆粒取代量大于10%時,對自密實混凝土的強度、抗凍性能及抗硫酸鹽干濕循環(huán)性能有明顯不利影響。
[Abstract]:The workability, compressive strength, stress-strain curve and freezing resistance of self-compacting concrete with different amount of rubber particles replacing fine aggregate with rubber particles were studied. The effect of sulphate resistance to wet and dry cycle and electric flux. The results show that rubber particles have great influence on the workability of fresh self-compacting concrete and the properties of hardened self-compacting concrete, and when the substitution amount of rubber particles is less than 15 (volume fraction), The addition of rubber particles can improve the workability of fresh self-compacting concrete, and the peak strain and ion permeation resistance of self-compacting concrete can be improved by rubber particles, when the substitution amount of rubber particles is more than 10, It has a significant negative effect on the strength, frost resistance and sulfate resistance of self-compacting concrete.
【作者單位】： 中南大學土木工程學院 高速鐵路建造技術國家工程實驗室 重載鐵路工程結構教育部重點實驗室;
【基金】：國家“973”計劃課題(2013CB036201) 國家自然科學基金(51178467,51108463) 教育部新世紀優(yōu)秀人才支持計劃(NCET-10-0839)項目資助
【分類號】：TU528

【參考文獻】

相關期刊論文 前10條

1 馬昆林;龍廣成;謝友均;;CRTSⅢ型板式無砟軌道充填層自密實混凝土碳化及力學性能演變的研究[J];鐵道科學與工程學報;2012年06期

2 王濤;洪錦祥;;橡膠混凝土的含氣量及其控制方法[J];混凝土與水泥制品;2009年03期

3 張亞梅;陳勝霞;高岳毅;;浸-烘循環(huán)作用下橡膠水泥混凝土的性能研究[J];建筑材料學報;2005年06期

4 郭永昌;劉鋒;陳貴炫;曾廣尚;劉豐;;橡膠混凝土的沖擊壓縮試驗研究[J];建筑材料學報;2012年01期

5 馮文賢;劉鋒;鄭萬虎;李麗娟;;橡膠混凝土疲勞性能的試驗研究[J];建筑材料學報;2012年04期

6 龍廣成;馬昆林;XIE Xu;謝友均;;橡膠集料對混凝土抗壓強度的降低效應[J];建筑材料學報;2013年05期

7 王開惠;朱涵;祝發(fā)珠;;橡膠集料砂漿試件抗硫酸鹽侵蝕性能初探[J];山東建筑大學學報;2007年01期

8 胡鵬;朱涵;王e，

本文編號：1825813