本文選題：膏體 + 抗離析性能�。� 參考：《中國礦業(yè)大學學報》2016年05期

【摘要】：通過建立骨料在料漿中的力學模型,確定粗骨料充填料漿具備良好抗離析性能的條件式M.運用三因素三水平正交實驗研究料漿飽和率為101.5%~105.3%時M值和離析率的取值范圍:以M=6作為料漿屈服應力在(200±25)Pa時的判定臨界值,可得相同條件下滿足飽和率要求的料漿M值范圍為2.3~4.2,從而得到適合工程應用、具備較好抗離析性能的料漿離析率為11.6%~17.8%.采用某礦固體物料按照現(xiàn)場參數(shù)充填料漿,對實驗結果進行實例驗證.結果表明:實例M值和離析率范圍與理論范圍吻合良好.離析率預測值與測量值相比,誤差分別為4.24%,1.09%,0.67%.
[Abstract]:By establishing the mechanical model of aggregate in slurry, the conditional formula M is determined that coarse aggregate filling slurry has good segregation resistance. Using three factors and three levels orthogonal experiment, the range of M value and segregation rate of slurry saturation ratio is 101.5 ~ 105.3.The critical value of yield stress of slurry is determined at 200 鹵25)Pa. Under the same conditions, the M value range of the slurry satisfying the saturation rate requirement is 2. 3 ~ 4. 2. Thus, the slurry segregation rate which is suitable for engineering application and has better anti-segregation performance is 11. 6% and 17. 8%. The experiment results are verified by using solid material in a mine to fill slurry according to field parameters. The results show that the range of M value and segregation rate are in good agreement with the theoretical range. Compared with the measured values, the deviation of the predicted segregation rate is 4.24 / 1.09 and 0.67, respectively.
【作者單位】： 北京科技大學金屬礦山高效開采與安全教育部重點實驗室;北京科技大學土木與環(huán)境工程學院;
【基金】：國家自然科學基金項目(51374034,51304011,51374035) 國家“十二五”科技支撐計劃項目(2012BAB08B02)
【分類號】：TD853.34

【相似文獻】

相關期刊論文 前1條

1 朱憲榮,王瑜,張風林,孫啟坡,王玉蘭;BB肥的生產[J];磷肥與復肥;2001年04期

相關會議論文 前2條

1 丁建彤;李渝軍;;泵送高強輕骨料混凝土的抗離析性能[A];2004“第七屆全國輕骨料混凝土學術討論會”暨“第一屆海峽兩岸輕骨料混凝土產制與應用技術研討會”論文集[C];2004年

2 何濤;趙青林;徐奇威;劉源強;馬磊;;高水灰比超細灌漿材料抗離析性能及干縮性能研究[A];第三屆全國商品砂漿學術交流會論文集[C];2009年

，

本文編號：1875461