本文選題：三點(diǎn)彎曲 + TiAl基合金　； 參考：《熱加工工藝》2015年24期

【摘要】：通過三點(diǎn)彎曲試驗(yàn)和掃描電鏡(SEM)斷口觀察研究了位移速率對(duì)具有全層微觀組織結(jié)構(gòu)TiAl基合金斷裂韌性及斷裂機(jī)理的影響。結(jié)果表明:全層組織斷裂韌性隨位移速率的提高而增加,全層組織試樣斷裂機(jī)理呈擴(kuò)展控制的特征,在較高的載荷速率加載時(shí),試樣的原始缺口起主導(dǎo)作用,主裂紋可沿正應(yīng)力最大的方向,選取直接快速的穿層方式擴(kuò)展;而在較低位移速率加載時(shí),主裂紋擴(kuò)展時(shí)有足夠時(shí)間沿結(jié)合能較低的層面擴(kuò)展。
[Abstract]:The effect of displacement rate on fracture toughness and fracture mechanism of TiAl-based alloy with full-layer microstructure was studied by means of three-point bending test and SEM (SEM) fracture. The results show that the fracture toughness of the whole layer increases with the increase of the displacement rate, and the fracture mechanism of the whole layer is controlled by expansion. When the loading rate is high, the original notch of the specimen plays a leading role. The main crack can be propagated directly and rapidly along the direction of the maximum normal stress, and when loading at lower displacement rate, there is sufficient time for the main crack to propagate along the plane with lower binding energy.
【作者單位】： 遼寧石油化工大學(xué)機(jī)械工程學(xué)院;蘭州理工大學(xué)甘肅省有色金屬新材料省部共建國(guó)家重點(diǎn)實(shí)驗(yàn)室;
【基金】：遼寧省博士基金(20131062)
【分類號(hào)】：TG115

【相似文獻(xiàn)】

相關(guān)期刊論文 前1條

1 梁新邦;鄭文龍;王春華;高怡斐;;關(guān)于GB/T 228.1-2010附錄F中應(yīng)變速率公式和橫梁位移速率公式的說明[J];理化檢驗(yàn)(物理分冊(cè));2014年06期

，

本文編號(hào)：2049437