本文選題：激光熔焊技術(shù)　切入點(diǎn)：模具失效　出處：《特種鑄造及有色合金》2015年12期

【摘要】：采用激光熔焊對(duì)有裂紋和磨損的A-MAX鋼壓鑄模具進(jìn)行模具修復(fù)與維護(hù),并對(duì)修復(fù)后的模具進(jìn)行微觀組織、拉伸性能和疲勞性能的分析。結(jié)果表明,激光熔焊接頭焊縫區(qū)存在細(xì)小的板條狀馬氏體以及一些沿晶界分布的白色鐵素體組織,接頭熱影響區(qū)組織為鐵素體和珠光體。經(jīng)過激光熔焊的模具的抗拉強(qiáng)度和伸長(zhǎng)率達(dá)到全新A-MAX模具的93.95%和88.92%,而且修復(fù)后模具的疲勞壽命也得到明顯改善,與全新模具的疲勞循環(huán)次數(shù)在同一個(gè)數(shù)量級(jí)。
[Abstract]:The A-MAX die casting dies with cracks and wear were repaired and maintained by laser welding, and the microstructure, tensile properties and fatigue properties of the repaired dies were analyzed.The results show that there are fine lath martensite and some white ferrite microstructures distributed along grain boundaries in the weld zone of laser welding joint. The microstructure of the heat-affected zone of the joint is ferrite and pearlite.The tensile strength and elongation of the die welded by laser welding reach 93.95% and 88.92% of that of the new A-MAX mould, and the fatigue life of the repaired die is improved obviously, which is in the same order of magnitude as that of the new mould.
【作者單位】： 浙江工業(yè)職業(yè)技術(shù)學(xué)院;
【基金】：浙江省教育廳科研項(xiàng)目(FW2013096)
【分類號(hào)】：TG456.7;TG241

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 何則榮;間歇疲勞——(Ⅰ)卸幅靜載間歇對(duì)軟鋼疲勞的影響[J];福州大學(xué)學(xué)報(bào);1984年02期

2 查傳元,周則恭;帶裂紋球罐疲勞壽命的概率分析[J];太原重型機(jī)械學(xué)院學(xué)報(bào);1984年02期

3 王金瑞,李益民;工程高溫部件疲勞壽命予測(cè)方法[J];熱力發(fā)電;1984年05期

4 王世俊,宋新玉,潘秀麗;真空脫氣軸承鋼的疲勞壽命及影響因素[J];機(jī)械工程材料;1985年04期

5 趙鐘會(huì);萬業(yè)恕;游泳;王昌生;張繼咸;王世俊;宋新玉;潘秀麗;;軸承鋼接觸疲勞壽命及其影響因素的回歸分析[J];特殊鋼;1985年02期

6 劉崇明,陳方明;利用鈣和稀土元素提高汽車彈簧鋼疲勞壽命的研究[J];稀土;1987年06期

7 王成國;王世清;喬毅南;;淬火油溫度對(duì)零件接觸疲勞壽命的影響[J];金屬熱處理;1987年08期

8 張棟;渦輪葉片剩余疲勞壽命直接估算方法探討[J];機(jī)械工程材料;1989年01期

9 張樹松;勇蘋;周淑蘭;仝愛蓮;;由改善顯微組織形態(tài)提高鋼件疲勞壽命[J];西安工業(yè)大學(xué)學(xué)報(bào);1989年02期

10 衡莉瓊;施愛國;;氧含量對(duì)齒輪鋼材料接觸疲勞壽命的影響[J];二汽科技;1990年02期

相關(guān)會(huì)議論文 前9條

1 王，

本文編號(hào)：1712598