【摘要】：通過改變長脈沖激光輸出功率和脈寬,在304L不銹鋼表面加工出凹坑、凸包微織構(gòu),并觀察了它們的形貌特征。研究結(jié)果表明,利用小脈寬、大功率激光可加工得到外形較好的凹坑,脈寬不變時,凹坑深度和直徑隨功率的增加呈先上升后下降的趨勢。然而,大脈寬、小功率激光加工可得到外形較好的凸包,功率對凸包形貌的影響比脈寬的影響大,當功率達到一定值時,凸包高度和直徑達到飽和狀態(tài)。
[Abstract]:By changing the output power and pulse width of long pulse laser, pits and convexity microtextures were fabricated on the surface of 304L stainless steel, and their morphologies were observed. The results show that the pits with good shape can be obtained by using small pulse width and high power laser. When the pulse width is constant, the depth and diameter of the pits increase first and then decrease with the increase of power. However, large pulse width, low power laser processing can obtain a better shape of convex hull, the influence of power on the shape of convex hull is greater than that of pulse width. When the power reaches a certain value, the height and diameter of convex hull reach saturation state.
【作者單位】： 南京農(nóng)業(yè)大學工學院;
【基金】：江蘇省自然科學基金青年基金(BK20150685) 中央高�；究蒲袠I(yè)務費(KYZ201659) 南京農(nóng)業(yè)大學工學院優(yōu)秀青年人才科技基金(YQ201604)
【分類號】：TG665

【相似文獻】

相關(guān)期刊論文 前2條

1 秦淵;倪曉武;陳彥北;;長脈沖激光致鋁合金靶產(chǎn)生熱應力的數(shù)值研究[J];紅外與激光工程;2008年S3期

2 ;[J];;年期

相關(guān)會議論文 前1條

1 秦淵;倪曉武;陳彥北;;長脈沖激光致鋁合金靶產(chǎn)生熱應力的數(shù)值研究[A];2008年激光探測、制導與對抗技術(shù)研討會論文集[C];2008年

相關(guān)碩士學位論文 前8條

1 王洋;長脈沖激光與金屬相互作用分析[D];長春理工大學;2008年

2 竇如鳳;長脈沖激光致介質(zhì)薄膜損傷機理與閾值測量研究[D];南京理工大學;2009年

3 張一鳴;長脈沖激光致金屬熔融噴濺的理論研究[D];南京理工大學;2013年

4 付耀龍;長脈沖激光輻照硅材料的損傷研究[D];長春理工大學;2013年

5 張梁;長脈沖激光與半導體材料的熱作用的數(shù)值分析[D];南京理工大學;2007年

6 范子嘉;長脈沖激光與金屬相互作用的熱分析[D];長春理工大學;2010年

7 李政;重復頻率長脈沖激光作用光學玻璃的熱特性研究[D];長春理工大學;2013年

8 王冰;長脈沖激光輻照金屬鋁LY12的溫度場與應力場研究[D];長春理工大學;2014年

，

本文編號：2199450