本文選題：Ti　切入點：Al合金　出處：《稀有金屬材料與工程》2016年09期 　論文類型：期刊論文

【摘要】：粉末冶金可以避免鑄錠冶金過程中出現(xiàn)的宏觀偏析、枝晶偏析、化學成分不均勻、組織不一致等缺陷,是制備TiA l合金的重要方法。本文綜述了近年來國內(nèi)外TiA l合金粉末冶金的研究進展,介紹了預合金法、元素粉末法和機械合金化法3種TiA l粉末制備方法及其各自的燒結方法。同時評述了各燒結方法的優(yōu)缺點及其制備合金的力學性能,并指出了粉末冶金制備TiA l合金今后有待改善的研究方向。
[Abstract]:Powder metallurgy can avoid the defects such as macrosegregation, dendrite segregation, chemical composition inhomogeneity and structure inconsistency in the process of ingot metallurgy. It is an important method to prepare TiA l alloy. In this paper, the research progress in powder metallurgy of TiA l alloy at home and abroad is reviewed, and the prealloying method is introduced. Element powder method and mechanical alloying method were used to prepare TiA l powder and their respective sintering methods. The advantages and disadvantages of each sintering method and the mechanical properties of the prepared alloy were also reviewed. The future research direction of TiA l alloy prepared by powder metallurgy is pointed out.
【作者單位】： 哈爾濱工業(yè)大學金屬精密熱加工國家級重點實驗室;
【基金】：新金屬材料國家重點實驗室開放基金(2013-ZD06) 國家自然科學基金(51471056) 國家重點基礎研究發(fā)展計劃(“973”計劃)(2011CB605502)
【分類號】：TG146.23;TF12

【相似文獻】

相關期刊論文 前10條

1 ;力學性能二級人員取證復習參考題(之一)解答[J];理化檢驗(物理分冊);1997年12期

2 ;力學性能二級人員取證復習參考題(之三)解答[J];理化檢驗(物理分冊);1998年04期

3 陳金寶;高溫力學性能二級人員取證復習參考題(持久部分之五)解答[J];理化檢驗(物理分冊);2000年02期

4 潘葉金;電弧熔鑄的Nb-18Si-5Mo-5Hf-2C復合材料的力學性能[J];中國鉬業(yè);2003年03期

5 張美忠,李賀軍,李克智;三維編織復合材料的力學性能研究現(xiàn)狀[J];材料工程;2004年02期

6 游宇,周新貴;三維編織復合材料的力學性能[J];纖維復合材料;2004年04期

7 羅文波;唐欣;譚江華;趙榮國;;流變材料長期力學性能加速表征的若干進展[J];材料導報;2007年07期

8 嚴振宇;徐強;朱時珍;劉穎;;Sm_2Zr_2O_7-ZrB_2/SiC復合材料的制備及力學性能研究[J];稀有金屬材料與工程;2011年S1期

9 瞿欣;孫汝n，

本文編號：1568807