【摘要】：采用高溫高壓及電化學(xué)腐蝕實(shí)驗(yàn)研究了Q235鋼、13Cr以及Q235鋼表面沉積Ni Cr Al涂層后的耐CO2腐蝕性能。Ni Cr Al涂層采用等離子噴涂制備。結(jié)果表明:Q235鋼抗均勻腐蝕和局部腐蝕的能力較差;13Cr抗均勻腐蝕能力良好,但出現(xiàn)明顯的點(diǎn)蝕;Ni Cr Al涂層具有良好的抗均勻腐蝕及點(diǎn)蝕能力。Ni Cr Al涂層的通孔結(jié)構(gòu)為腐蝕介質(zhì)提供了滲入通道,進(jìn)而腐蝕界面處的Q235鋼。
[Abstract]:The corrosion resistance of NiCrAl coating on Q235 steel and Ni-CrAl coating on Q235 steel was studied by high temperature and high pressure and electrochemical corrosion experiments. The results showed that the corrosion resistance of Q235 steel was uniform and local. The ability of corrosion is poor and the uniform corrosion resistance of 13Cr is good. But the obvious pitting corrosion of Ni Cr Al coating has good resistance to uniform corrosion and pitting corrosion. The through pore structure of Ni Cr Al coating provides an infiltration channel for corrosion medium and then corrodes Q235 steel at the interface.
【作者單位】： 西安石油大學(xué)材料科學(xué)與工程學(xué)院;
【基金】：國家自然科學(xué)基金資助項(xiàng)目(51605384) 陜西省自然科學(xué)基礎(chǔ)研究計(jì)劃項(xiàng)目(2016JQ5077) 陜西省教育廳專項(xiàng)科研計(jì)劃項(xiàng)目(16JK1597) 西安石油大學(xué)《材料科學(xué)與工程》省級優(yōu)勢學(xué)科資助(YS37020203)
【分類號】：TG174.4

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 李行志,胡樹兵;等離子噴涂的發(fā)展及其應(yīng)用[J];湖北汽車工業(yè)學(xué)院學(xué)報(bào);2004年02期

2 陳麗梅;李強(qiáng);;等離子噴涂技術(shù)現(xiàn)狀及發(fā)展[J];熱處理技術(shù)與裝備;2006年01期

3 ;武漢材保所：重新啟用高能等離子噴涂設(shè)備 為建設(shè)“兩型”社會(huì)作貢獻(xiàn)[J];表面工程資訊;2008年02期

4 ;等離子噴涂設(shè)備簡介[J];材料保護(hù);1966年04期

5 ;等離子噴涂[J];機(jī)車車輛工藝;1971年05期

6 高奉周;;大功率等離子噴涂槍鑒定會(huì)在沈陽舉行[J];焊接;1980年06期

7 耿家林;;等離子噴涂修復(fù)發(fā)動(dòng)機(jī)傳動(dòng)桿[J];航空工藝技術(shù);1981年07期

8 谷式，

本文編號：1563950