本文選題：機制砂 + 石粉�。� 參考：《水運工程》2017年09期

【摘要】：劈裂抗拉強度是評價混凝土抗裂性能重要的力學指標,試驗分析砂巖機制砂石粉含量對混凝土劈裂抗拉強度影響及機理。結(jié)果表明:砂巖機制砂中石粉含量對不同強度等級混凝土的工作性、劈裂抗拉強度影響不同,對C35和C45強度等級的機制砂混凝土,當機制砂中石粉含量為7%~13%和5%~8%時,隨石粉含量的增加,新拌混凝土和易性得到改善,混凝土抗壓強度及劈裂抗拉強度不斷提高;建立砂巖機制砂混凝土劈裂抗拉強度與抗壓強度之間的數(shù)學公式:lg f_(sp)=0.309 7lg f_(cu)+0.102 6,機制砂混凝土的劈裂抗拉強度優(yōu)于普通混凝土,具有更為優(yōu)異的抗裂性能。機制砂石粉的顆粒效應、化學活性是機制砂混凝土劈裂抗拉性能的主要影響因素。
[Abstract]:The splitting tensile strength is an important mechanical index to evaluate the crack resistance of concrete. The effect and mechanism of sandstone mechanism sand powder content on the splitting tensile strength of concrete are analyzed experimentally. The results show that the content of stone powder in the sand has different effects on the workability and splitting tensile strength of concrete with different strength grades. For the concrete with C35 and C45 strength grades, when the content of stone powder in the sand is 7% and 5 ~ 8%, With the increase of the content of stone powder, the readability of fresh concrete is improved, and the compressive strength and splitting tensile strength of concrete are improved. The mathematical formula between splitting tensile strength and compressive strength of sandstone machine-made sand concrete is established. The splitting tensile strength of machine-made sand concrete is better than that of ordinary concrete, and it has better crack resistance performance than that of ordinary concrete. The particle effect and chemical activity of machine-made sand and stone powder are the main factors influencing the splitting and tensile properties of machine-made sand concrete.
【作者單位】： 中交四航局第一工程有限公司;水工構(gòu)造物耐久性技術交通行業(yè)重點實驗室中交四航工程研究院有限公司;
【分類號】：TU528

【相似文獻】

相關期刊論文 前6條

1 金鑫;杜紅秀;閻蕊珍;;高性能混凝土高溫后劈裂抗拉強度試驗研究[J];太原理工大學學報;2013年05期

2 孫正甫;袁英杰;王超;王強;閻培渝;;不同礦物摻合料對高強混凝土劈裂抗拉強度的影響差異[J];混凝土;2014年03期

3 周靜海;劉子赫;李婷婷;楊永生;;廢棄纖維再生混凝土的劈裂抗拉強度試驗[J];沈陽建筑大學學報(自然科學版);2013年05期

4 張廷毅;汪自力;朱海堂;鄭光和;;多因素影響下銑削型鋼纖維混凝土劈裂抗拉強度[J];建筑材料學報;2014年03期

5 周梅;白金婷;張曉帆;;橡膠粉摻量及粗細度對混凝土強度影響的數(shù)學分析[J];工業(yè)建筑;2011年09期

6 馮秀平,楊南如;CaO-SiO_2-P_2O_5-H_2O 系統(tǒng)中 CBC 材料的原料配比研究[J];河海大學學報;1998年01期

，

本文編號：1832002