本文選題：化學(xué)鋼化 + 離子交換時(shí)間　； 參考：《硅酸鹽通報(bào)》2016年06期

【摘要】：本文主要研究化學(xué)鋼化玻璃中第一步離子交換的時(shí)間對(duì)化學(xué)鋼化玻璃的性能影響。制備出不同的離子交換時(shí)間的化學(xué)鋼化玻璃。分析第一步交換時(shí)間對(duì)鋼化玻璃的彎曲強(qiáng)度、Weibull模數(shù)、表面應(yīng)力大小、深度以及K+離子擴(kuò)散所產(chǎn)生的影響。結(jié)果表明:隨著第一步離子交換時(shí)間的延長,彎曲強(qiáng)度逐漸降低,Weibull先升高后降低,在40h時(shí)達(dá)到最高值;表面應(yīng)力大小會(huì)隨著時(shí)間的延長而降低,應(yīng)力深度會(huì)增加;K+離子擴(kuò)散曲線符合菲克第二定律的擬合曲線。擴(kuò)散深度隨著時(shí)間增加而增加,并且會(huì)在玻璃內(nèi)部產(chǎn)生富集峰。
[Abstract]:The effect of the first step ion exchange time on the properties of chemically toughened glass was studied in this paper.Chemical toughened glass with different ion exchange time was prepared.The effects of the first step exchange time on the bending strength Weibull modulus, surface stress, depth and K ion diffusion of toughened glass are analyzed.The results show that with the prolongation of the first step ion exchange time, the bending strength of Weibull increases first and then decreases, and reaches the maximum value at 40 h, and the surface stress decreases with the time.The stress depth increases the fitting curve of K ion diffusion curve in accordance with Fick's second law.The diffusion depth increases with time, and the enrichment peak occurs in the glass.
【作者單位】： 武漢理工大學(xué)材料科學(xué)與工程學(xué)院;武漢理工大學(xué)硅酸鹽建筑材料國家重點(diǎn)實(shí)驗(yàn)室;
【基金】：“十二五”國家科技支撐計(jì)劃(2012BAA08B04)資助
【分類號(hào)】：TQ171.732

【相似文獻(xiàn)】

相關(guān)期刊論文 前6條

1 郭宏武;付定軍;郭宏偉;;組成對(duì)銅離子擴(kuò)散著色玻璃光譜性能的影響研究[J];玻璃;2009年01期

2 丁習(xí);光和聲測定增強(qiáng)玻璃的性能[J];玻璃與搪瓷;1973年04期

3 青格樂圖;宋士強(qiáng);范永生;王保國;;質(zhì)子傳導(dǎo)膜內(nèi)受限空間離子擴(kuò)散過程[J];化工學(xué)報(bào);2013年02期

4 王承遇;關(guān)于玻璃化學(xué)鋼化問題的探討[J];玻璃;1982年03期

5 劉子建;趙軒;孟祥鋒;;鋁與玻璃的多層鍵合[J];中國新技術(shù)新產(chǎn)品;2012年06期

6 ;[J];;年期

，

本文編號(hào)：1771912