本文選題：動(dòng)態(tài)劈裂試驗(yàn)　切入點(diǎn)：高強(qiáng)混凝土　出處：《河南科技大學(xué)學(xué)報(bào)(自然科學(xué)版)》2017年01期

【摘要】：以圓形紫銅片作為波形整形器,利用直徑100 mm的霍普金森壓桿裝置,研究了不同彈速?zèng)_擊下高強(qiáng)混凝土平臺巴西圓盤試件的動(dòng)態(tài)拉伸強(qiáng)度,得到了高強(qiáng)混凝土在沖擊作用下的劈裂強(qiáng)度、破壞模式和應(yīng)力時(shí)程曲線。試驗(yàn)結(jié)果表明:隨著沖擊應(yīng)變率的提高,高強(qiáng)混凝土試件的動(dòng)態(tài)劈裂強(qiáng)度和破壞程度不斷增大,具有顯著的應(yīng)變率敏感性。高速?zèng)_擊荷載下的混凝土斷面區(qū)較為光滑,裂縫直接穿過石子導(dǎo)致試樣斷裂。
[Abstract]:The dynamic tensile strength of Brazilian disk specimens of high strength concrete platform under different impact velocities was studied by using a 100 mm Hopkinson compression bar with a circular copper sheet as a waveform shaper. The splitting strength, failure mode and stress time history curves of high strength concrete under impact are obtained. The experimental results show that the dynamic splitting strength and failure degree of high strength concrete specimens increase with the increase of impact strain rate. The concrete section under high speed impact load is smooth, and the crack directly through the stone leads to the fracture of the specimen.
【作者單位】： 桂林理工大學(xué)土木與建筑工程學(xué)院;北海藝術(shù)設(shè)計(jì)學(xué)院建筑學(xué)院;
【基金】：國家自然科學(xué)基金項(xiàng)目(51568016) 廣西礦冶與環(huán)境科學(xué)實(shí)驗(yàn)中心項(xiàng)目(KH2011YB025)
【分類號】：TU528