本文選題：鎢基　切入點：陶瓷　出處：《人工晶體學報》2017年09期

【摘要】：本文通過對鎢基陶瓷結(jié)晶釉材料進行了快速結(jié)晶制備,所得釉層晶相為WOP2O7結(jié)構(gòu)。通過掃描電鏡分析發(fā)現(xiàn)其表面具有顯著地結(jié)晶化特征形貌,進一步結(jié)合EDS能譜分析發(fā)現(xiàn)其表面形貌有鎢基結(jié)晶釉相和底釉相兩種結(jié)構(gòu)構(gòu)成。在光催化性能探索中發(fā)現(xiàn)該釉層材料在紫外可見光照射下展現(xiàn)出一定的催化降解羅丹明B溶液的能力,為陶瓷結(jié)晶釉材料的功能化價值提升提供了參考。
[Abstract]:In this paper, the crystalline glaze of tungsten based ceramics was prepared by rapid crystallization. The crystalline phase of the glaze layer was characterized by WOP2O7 structure. The morphology of crystalline glaze on the surface was found to be remarkably crystallized by scanning electron microscopy (SEM). In combination with EDS energy spectrum analysis, it was found that the surface morphology of the glaze was composed of tungsten based crystalline glaze phase and bottom glaze phase. In the exploration of photocatalytic properties, it was found that the glaze layer exhibited a certain catalytic degradation under ultraviolet and visible light irradiation. The ability of Rhodamine B solution, It provides a reference for improving the function value of ceramic crystalline glaze material.
【作者單位】： 陜西科技大學材料科學與工程學院;廣東蒙娜麗莎新型材料集團有限公司;
【基金】：陜省教育廳專項科研計劃項目(15JK1074)
【分類號】：O643.36;O644.1;TQ174.43

【相似文獻】

相關(guān)碩士學位論文 前1條

1 韓帥;Ag/ZnO及CdS/ZnO納米復(fù)合結(jié)構(gòu)的光催化性能研究[D];鄭州大學;2017年

，

本文編號：1661782