本文選題：支撐體　切入點(diǎn)：碳化硅　出處：《中國(guó)陶瓷》2017年10期 　論文類型：期刊論文

【摘要】：采用碳化硅為骨料,膨潤(rùn)土、甲基纖維素、滑石粉、活性炭等為添加劑制作多孔材料。通過(guò)電子顯微鏡掃描、抗彎抗壓測(cè)試等技術(shù),對(duì)材料孔隙率、通透率、抗彎抗壓強(qiáng)度、微觀形貌等進(jìn)行分析。結(jié)果表明,當(dāng)壓制壓力1.5 MPa,燒結(jié)溫度1300℃,配比為膨潤(rùn)土5%,甲基纖維素5%,滑石粉5%,活性炭6%,所得樣品孔隙率可達(dá)43.5%,純水通量約為13.2m~3/m~2·h,抗彎強(qiáng)度可以保持在13 MPa左右。
[Abstract]:Porous materials were prepared by using silicon carbide as aggregate, bentonite, methyl cellulose, talc powder and activated carbon as additives. The results show that when the pressing pressure is 1.5 MPA, the sintering temperature is 1300 鈩，