本文選題：晶體結(jié)構(gòu) + X射線衍射��； 參考：《低溫物理學(xué)報》2017年05期

【摘要】：利用GN-2型高能球磨機(jī)研磨了Y_2O_3粉末晶體,用BT-1600圖像顆粒分析儀對研磨時間為0h和20h的兩份樣品進(jìn)行了分析.室溫條件下,利用X射線衍射實驗檢測了晶體結(jié)構(gòu)的變化,并且利用RIETAN-2000程序進(jìn)行了晶體結(jié)構(gòu)精修得到了原子熱振動的大小.運(yùn)用MEM解析方法實現(xiàn)了2D(平面)和3D(立體)的等高電子密度分布的可視化.
[Abstract]:Yap _ 2O _ 3 powder crystal was ground by GN-2 high-energy ball mill. Two samples with grinding time of 0h and 20h were analyzed by BT-1600 image particle analyzer. At room temperature, X-ray diffraction experiments were used to detect the changes of crystal structure, and the size of atomic thermal vibration was obtained by refinement of crystal structure using RIETAN-2000 program. The visualization of 2D (plane) and 3D (stereoscopic) iso-high electron density distribution is realized by means of MEM analytic method.
【作者單位】： 內(nèi)蒙古民族大學(xué)物理與電子信息學(xué)院;
【基金】：內(nèi)蒙古自治區(qū)自然科學(xué)基金面上項目(2014MS0109) 內(nèi)蒙古自治區(qū)留學(xué)回區(qū)人員小額資助經(jīng)費(fèi)項目資助的課題~~
【分類號】：O614.322;O76

【相似文獻(xiàn)】

相關(guān)期刊論文 前1條

1 張子高;;原子-分子理論的歷史發(fā)展[J];化學(xué)通報;1957年09期

，

本文編號：2001020