本文選題：聚羧酸 + 減水劑��； 參考：《化學研究與應用》2017年12期

【摘要】：通過相互復滲技術(shù)將自制的聚酯型(PCS-1)和聚醚型(PCS-2)兩類減水劑母液復配,系統(tǒng)地研究了兩組分摻量變化對其性能的影響。利用傅立葉變換紅外光譜儀(FTIR)、X射線衍射(XRD)、熱重(TG-DTG)和比表面(BET)研究了加入復配母液的硬化水泥石微觀結(jié)構(gòu)。結(jié)果表明,復配母液減水劑的加入促進了水泥水化,減小了水泥石的比表面積、孔容和孔徑。
[Abstract]:The self-made polyether type (PCS-1) and polyether type (PCS-2) two type water reducer was mixed with each other, and the effects of the two components on the properties of the two type water reducing agent were systematically studied. The hardened cement stones added to the compound mother liquid were studied by using the Fu Liye transform infrared spectrometer (FTIR), X ray diffraction (XRD), thermogravimetric (TG-DTG) and specific surface (BET). The results showed that the addition of water reducing agent of compound mother liquor promoted the hydration of cement and reduced the specific surface area of cement paste, Kong Rong and pore size.
【作者單位】： 河套學院農(nóng)學系;內(nèi)蒙古大學化學化工學院;河套學院理學系;
【基金】：內(nèi)蒙古自治區(qū)高等學校科學研究項目(NJZY16337)資助 河套學院科學技術(shù)研究青年項目(HYZQ201411)資助
【分類號】：TQ172.1

【相似文獻】

相關(guān)期刊論文 前8條

1 龔英;段國榮;黃國泓;;新型聚羧酸系保塑劑的性能研究[J];新型建筑材料;2010年11期

2 趙寶龍;;聚羧酸高性能外加劑(聚羧酸系減水劑)在客運專線工程中的應用[J];中國新技術(shù)新產(chǎn)品;2011年04期

3 畢化泗;孫延慶;湯樂豐;李柱;;砂對應用聚羧酸的商品混凝土的性能影響[J];廣東建材;2012年09期

4 廖國勝;何正戀;劉佩;;新型聚羧酸系保坍劑的合成與性能研究[J];建材世界;2013年04期

5 廖秋林;郎春林;廖聲金;;改性醚類聚羧酸超塑化劑的制備及性能研究[J];商品混凝土;2012年07期

6 邵強;雷翅;;一種高適應性聚羧酸保坍劑的制備及性能研究[J];廣州建筑;2014年02期

7 郭鑫祺;;環(huán)保交聯(lián)型聚羧酸專用保坍劑的合成與性能研究[J];新型建筑材料;2013年05期

8 陳軍超;蔡其全;李萍;陳軍磊;;聚羧酸系高性能混凝土外加劑的應用[J];中國高新技術(shù)企業(yè);2012年13期

相關(guān)會議論文 前2條

1 陳國新;祝燁然;沈燕平;黃國泓;;聚羧酸系保坍劑的一步法合成及性能[A];中國建筑材料聯(lián)合會混凝土外加劑分會第十四次會員代表大會--“科隆杯”混凝土外加劑論文集（上冊）[C];2014年

2 林榮峰;常青山;王敏;付鵬;劉振華;;具有多種官能團聚羧酸高效減水劑的研制[A];中國建筑材料聯(lián)合會混凝土外加劑分會第十四次會員代表大會--“科隆杯”混凝土外加劑論文集（上冊）[C];2014年

相關(guān)碩士學位論文 前2條

1 肖煜;聚羧酸系高性能保坍劑的研究[D];武漢科技大學;2013年

2 毛玉成;聚羧酸大分子的合成及其在模具石膏中的應用[D];江南大學;2014年

，

本文編號：2084157