文獻(xiàn)名稱：納米二氧化硅的改性及其在丁基橡膠中應(yīng)用研究

    前言：該文研究了、改性納米二氧化硅和未的表面自由能分析了改性納米二氧化硅與未硫化增強(qiáng)膠的相容性。 研究了納米二氧化硅用量對硫化膠力學(xué)性能的影響,隨著納米二氧化硅填充量的增加,結(jié)合橡膠中共價鍵作用的貢獻(xiàn)增加,硫化膠總交聯(lián)密度增加,化學(xué)交聯(lián)密度在填充量2.0%時增至最大然后緩慢降低。應(yīng)用實(shí)驗(yàn)表明,硫化膠中填充1.0%的改性納米二氧化硅,硫化膠的拉伸強(qiáng)度為8.22MPa,拉斷伸長率提高到823.15%;納米二氧化硅填充量增加至3.5%,拉伸強(qiáng)度增至9.28MPa,拉斷伸長率下...
    In the paper, Nano-silica is treated with Vinyl-silane A-151, which has a good hydrophobic. The surface status of nano-silica before and after modification was studied. It is verified that modification of nano-silica can be carried out by this technics and the aggregation of nano-silica can be dispersed effectively. Lipophilic degree and surface silanol groups of modified nano-silica were measured by titration. The effect of modification of modified nano-silica was discussed by analysising activation t...

文獻(xiàn)名稱 納米二氧化硅的改性及其在丁基橡膠中應(yīng)用研究

Article Name
英文(英語)翻譯 Surface Modification of Nano-SiO_2 and It's Application Study in Butyl Rubber;

作者 歐陽兆輝; 導(dǎo)師:伍林;

Author

作者單位
Author Agencies 武漢科技大學(xué);

文獻(xiàn)出處
Article From 中國科學(xué)院上海冶金研究所; 材料物理與化學(xué)(專業(yè)) 博士論文 2000年度

關(guān)鍵詞 納米二氧化硅; 表面改性; 硅烷偶聯(lián)劑; 硫化膠; 溶解度參數(shù);

Keywords nano-silica;surface modification;silicane agents;vulcanizes;solubility parameter;

KH-550改性納米二氧化硅的研究
聚乳酸/納米二氧化硅原位復(fù)合材料的制備和性能
羧甲基纖維素納米二氧化硅復(fù)合物制備及其結(jié)晶行為
納米二氧化硅填充PVDF聚合物微孔膜的研究
熱鍍鋅鋼板納米二氧化硅改性有機(jī)-無機(jī)復(fù)合膜
單分散納米二氧化硅的制備與表征
巰丙基功能化介孔納米二氧化硅的合成
溶膠-沉淀法疏水納米二氧化硅的制備及其在硅橡膠中的應(yīng)用
聚乙烯醇/納米二氧化硅復(fù)合薄膜的制備及性能
納米二氧化硅改性激光全息涂料的性能研究

  本文關(guān)鍵詞：納米二氧化硅的改性及其在丁基橡膠中應(yīng)用研究，由筆耕文化傳播整理發(fā)布。