本文選題：玻璃粉末 + 摻量��； 參考：《混凝土》2017年11期

【摘要】：廢棄玻璃經破碎研磨后具有火山灰活性,將其用作水泥混凝土摻合料具有良好的性能,并且有利于減少二氧化碳的排放。目前國內對此種材料用法研究甚少,國外的研究也較為零散。整理分析了國內外學者的相關研究數(shù)據(jù),分析了玻璃粉末摻合料的物理化學特性,研究了該種水泥所制混凝土的力學性能,并分析了摻量,養(yǎng)護齡期和養(yǎng)護溫度的影響,得出最佳的玻璃粉末摻合料摻量范圍為20%~25%。對于推動國內玻璃粉末摻合料在水泥混凝土中應用具有積極作用。
[Abstract]:The waste glass has pozzolanic activity after crushing and grinding, it has good performance as cement concrete admixture, and it is helpful to reduce carbon dioxide emission. At present, there are few studies on the use of this material in China, and more scattered research abroad. The related research data of domestic and foreign scholars are analyzed, the physical and chemical properties of glass powder admixture are analyzed, the mechanical properties of concrete made by this kind of cement are studied, and the influence of the amount of cement, curing age and curing temperature on the concrete is analyzed. The optimum range of glass powder admixture is 20% 25%. It plays an active role in promoting the application of glass powder admixture in cement concrete.
【作者單位】： 上海交通大學船舶海洋與建筑工程學院;英國伯明翰大學機械與土木工程學院;
【分類號】：TU528

【相似文獻】

相關期刊論文 前10條

1 孫志剛;我國摻合料及摻合料技術現(xiàn)狀和展望[J];中國水泥;2004年11期

2 陳建輝;;摻合料在混凝土生產中的應用[J];廣東建材;2012年07期

3 劉雅琦;阮炯正;仲崇山;孫英嬌;;混凝土礦物復合摻合料應用技術規(guī)范的探討[J];吉林建筑工程學院學報;2013年02期

4 趙學明;張曉平;尹友非;張浦陽;;有摻合料高強、超高強高性能混凝土的試驗結果與分析[J];混凝土;2013年06期

5 張德娟;徐虎;郭立偉;劉險峰;;摻加摻合料高強高性能混凝土的材料性能試驗研究[J];新疆大學學報(自然科學版);2006年02期

6 劉志國;劉紅霞;楊少偉;;水泥摻合料分析對混凝土配合比設計的重要性[J];混凝土;2012年09期

7 錢大行;孫犁;張日華;;再生磨細摻合料的研制和應用[J];混凝土;2008年09期

8 趙國成;牛亞林;李永亮;;綠色復合摻合料在混凝土中的實驗與生產應用[J];四川建材;2014年03期

9 袁永福;金高峰;蘭燕紅;;摻合料在混凝土中最佳組合和影響的試驗研究[J];基建優(yōu)化;2006年01期

10 星武 ,段艷;資中研制成功水泥助磨摻合料[J];內江科技;2003年01期

相關會議論文 前8條

1 向安樂;袁紅星;;復合摻合料在預應力高強混凝土管樁生產中的應用[A];中國混凝土與水泥制品協(xié)會2012年會論文集[C];2012年

2 張德娟;徐虎;郭立偉;劉險峰;;摻加摻合料高強高性能混凝土的材料性能試驗研究[A];全國高性能混凝土和礦物摻合料的研究與工程應用技術交流會論文集[C];2006年

3 沈Z醚，

本文編號：1828637