本文關(guān)鍵詞： 重結(jié)晶碳化硅 抗氧化性 抗熱震性 高溫強度 窯具　出處：《耐火材料》2017年01期 　論文類型：期刊論文

【摘要】：從原料純度及顆粒形狀、成型方法、燒結(jié)溫度及燒結(jié)氣氛等方面闡述了重結(jié)晶碳化硅材料的制備工藝及其特點,并與其他組成或性能相近的碳化硅材料做了對比;介紹了重結(jié)晶碳化硅材料的組成、結(jié)構(gòu)與性能特點,重點介紹了重結(jié)晶碳化硅材料在高溫強度、抗氧化性等方面的研究,并概述了重結(jié)晶碳化硅材料在高溫窯具、柴油車尾氣凈化器等領(lǐng)域的應用情況。
[Abstract]:The preparation process and characteristics of recrystallized silicon carbide are described from aspects of raw material purity and particle shape, molding method, sintering temperature and sintering atmosphere, and compared with other silicon carbide materials with similar composition or properties. The composition, structure and properties of recrystallized silicon carbide materials are introduced. The research on high temperature strength and oxidation resistance of recrystallized silicon carbide materials is introduced, and the application of recrystallized silicon carbide materials in high temperature kiln furniture is summarized. Diesel vehicle exhaust purifier and other areas of application.
【作者單位】： 中鋼集團洛陽耐火材料研究院有限公司;
【分類號】：TQ127.2

【相似文獻】

相關(guān)期刊論文 前10條

1 李世斌,呂振林,高積強,金志浩;拓撲法計算硅/碳化硅材料的電阻率[J];中國有色金屬學報;2002年S1期

2 武七德,童元豐;碳化硅材料的氧化及抗氧化研究[J];陶瓷科學與藝術(shù);2002年01期

3 談國強,李建波;添加劑對二氧化硅包裹碳化硅材料性能的影響[J];佛山陶瓷;2004年03期

4 劉景林;利用碳化硅制造的耐磨復合材料[J];國外耐火材料;2005年04期

5 ;國外科技消息[J];陶瓷;1983年04期

6 譚澤全,唐鋼;碳化硅材料用于煉鋼[J];電爐;1989年03期

7 王潤澤，劉延伶;某些碳化硅材料的內(nèi)耗和熱震損傷[J];耐火材料;1996年02期

8 高積強,金志浩;碳化硅材料及其應用研究進展[J];粉末冶金材料科學與工程;1998年03期

9 李世斌,呂振林,高積強,金志浩;反應連接碳化硅材料接頭的力學和電性能[J];稀有金屬材料與工程;2003年08期

10 李世斌,李養(yǎng)良,金志浩;硅/碳化硅材料顯微特征與強度關(guān)系研究[J];陶瓷學報;2004年04期

相關(guān)會議論文 前10條

1 張崇宏;;不銹鋼與碳化硅材料中氦的行為研究[A];第一屆反應堆物理與核材料學術(shù)研討會論文摘要集[C];2004年

2 李世斌;茹紅英;馬明亮;金志浩;;熱處理條件對硅／碳化硅材料組織的影響[A];第十五屆華東地區(qū)熱處理年會暨華東地區(qū)熱處理年會三十周年紀念活動論文摘要集[C];2006年

3 李然;沈強;張聯(lián)盟;;短碳纖維復合碳化硅材料的燒結(jié)致密化研究[A];復合材料：生命、環(huán)境與高技術(shù)——第十二屆全國復合材料學術(shù)會議論文集[C];2002年

4 楊玉s，

本文編號：1530289