本文選題：激光技術(shù)　切入點(diǎn)：激光壓焊　出處：《中國激光》2017年06期

【摘要】：利用光纖激光掃描焊接鋁合金V型坡口,研究了坡口角度、透鏡焦距、離焦量等對(duì)坡口內(nèi)材料熔化行為的影響。結(jié)果表明,V型坡口對(duì)光纖激光具有明顯的匯聚作用。當(dāng)焦距為300mm、離焦量為0~10mm、坡口角度為5°時(shí),坡口內(nèi)可獲得較好的熔化效果。進(jìn)一步分析表明,這與鋁對(duì)光纖激光在布儒斯特角處的吸收率不高有關(guān),但由于每次反射會(huì)損失部分激光能量,因此光纖激光在V型坡口內(nèi)的反射次數(shù)不宜過多。
[Abstract]:The effects of groove angle, lens focal length and defocus on the melting behavior of aluminum alloy V-shaped groove were studied by using optical fiber laser scanning welding.The results show that V-groove has obvious convergent effect on fiber laser.When the focal length is 300 mm, the defocus is 0 ~ 10 mm and the groove angle is 5 擄, a better melting effect can be obtained in the groove.Further analysis shows that this is related to the low absorption rate of aluminum to fiber laser at Brewster corner, but due to the loss of part of laser energy in each reflection, the reflection times of fiber laser in V-shaped groove should not be excessive.
【作者單位】： 北京工業(yè)大學(xué)激光工程研究院高功率及超快激光先進(jìn)制造實(shí)驗(yàn)室;
【基金】：國家自然科學(xué)基金(51475011和51505011)
【分類號(hào)】：TG457.14;TN249

【相似文獻(xiàn)】

相關(guān)會(huì)議論文 前1條

1 張連新;;多功能導(dǎo)管擠壓焊封工程樣機(jī)研制[A];中國工程物理研究院科技年報(bào)：2013年版[C];2013年

相關(guān)碩士學(xué)位論文 前1條

1 宋厚寶;壓焊點(diǎn)晶體缺陷問題的程式優(yōu)化研究[D];上海交通大學(xué);2008年

，

本文編號(hào)：1715695