本文選題：偏高嶺土　切入點：地質(zhì)聚合物　出處：《長沙理工大學》2015年碩士論文　論文類型：學位論文

【摘要】：偏高嶺土基地質(zhì)聚合物材料作為無機材料,既具有有機材料、陶瓷、水泥等材料的優(yōu)良性能,又具有原材料豐富、工藝簡單、價格低廉、節(jié)約能源等優(yōu)點,與傳統(tǒng)水泥相比,具有節(jié)能、環(huán)保的特點,是潛在的一種綠色建筑材料。本文通過理論與試驗相結(jié)合對其進行性能研究,從而嘗試以偏高嶺土基地質(zhì)聚合物代替環(huán)氧樹脂應用于結(jié)構(gòu)的加固工程之中。本文研究工作的主要內(nèi)容如下:(1)將山西煤系高嶺土高溫煅燒活化之后得到的偏高嶺土與堿性激發(fā)劑混合得到偏高嶺土基地質(zhì)聚合物膠凝材料。通過正交試驗,研究改性水玻璃模數(shù)、激發(fā)劑摻量、固化溫度和固化時間對偏高嶺土基地質(zhì)聚合物膠凝材料的7d和28d強度的影響規(guī)律,最終遴選出最佳的配合比;通過極差分析,研究此四個因素對偏高嶺土基地質(zhì)聚合物膠凝材料7d和28d抗壓強度影響效果的強弱關(guān)系;(2)通過混凝土表層嵌貼FRP的單剪試驗,研究地質(zhì)聚合物無機膠黏劑和環(huán)氧樹脂有機膠黏劑經(jīng)高溫處理后的FRP-混凝土之間界面粘結(jié)性能。研究表明:環(huán)氧樹脂有機粘黏劑對高溫的敏感度要高于地質(zhì)聚合物無機粘黏劑,即隨著處理溫度的升高,環(huán)氧樹脂粘黏劑單剪試件的極限抗拉強度呈減弱趨勢,而地質(zhì)聚合物粘黏劑試件的極限抗拉強度無明顯變化;在此次試驗中,除了試件SK-120由于開槽處理不當出現(xiàn)膠層與混凝土之間的剝離破壞外,其余試件的破壞形態(tài)均為FRP與膠層之間的剝離破壞。
[Abstract]:As inorganic materials, metakaolin base polymer materials have the advantages of organic materials, ceramics, cement and so on, and have the advantages of abundant raw materials, simple technology, low price and energy saving. It is a potential green building material with the characteristics of energy saving and environmental protection. In order to try to replace epoxy resin with metakaolin base polymer in the strengthening project of structure. The main contents of this research work are as follows: 1) the kaolin of Shanxi coal measure after calcining and activating at high temperature to get partial kaolinite. The base polymer cementitious material of metakaolin is obtained by mixing soil with alkaline activator. The effects of modulus of modified sodium silicate, amount of activator, curing temperature and curing time on the strength of metakaolin base polymer cementitious material were studied. The influence of these four factors on the compressive strength of metakaolin base polymer cementitious materials was studied. The interfacial bond properties between geopolymer inorganic adhesives and epoxy resin organic adhesives treated at high temperature were studied. The results showed that the sensitivity of epoxy resin organic adhesives to high temperature was higher than that of geopolymer inorganic adhesives. That is, with the increase of treatment temperature, the ultimate tensile strength of the single shear specimen of epoxy resin adhesive tends to weaken, but the ultimate tensile strength of the geopolymer adhesive specimen does not change obviously. Except for the debonding failure between the rubber layer and concrete due to the improper slotted treatment of the specimen, the failure pattern of the other specimens is the peeling failure between the FRP and the rubber layer.
【學位授予單位】：長沙理工大學
【學位級別】：碩士
【學位授予年份】：2015
【分類號】：TU526

【參考文獻】

相關(guān)期刊論文 前10條

1 張婷婷;吳志堂;張鑫;;無機膠粘貼碳纖維布對鋼筋混凝土梁高溫性能的影響[J];溫州職業(yè)技術(shù)學院學報;2014年02期

2 楊濤;姚曉;張祖華;諸華軍;;NaOH溶液濃度及反應時間對偏高嶺土地質(zhì)聚合反應的影響[J];南京工業(yè)大學學報(自然科學版);2013年04期

3 饒紹建;王克儉;;高溫短期養(yǎng)護對低鈣粉煤灰地質(zhì)聚合物性能的影響[J];材料導報;2011年S1期

4 金漫彤;黃彩菊;邵江平;許杭俊;王連軍;;地聚物固化體抗高溫性能及數(shù)學模型研究[J];浙江工業(yè)大學學報;2011年01期

5 饒紹建;王克儉;;正交試驗研究礦物聚合物抗壓強度[J];硅酸鹽通報;2010年06期

6 王晴;丁兆洋;賀天姝;陳彥文;;地聚合物混凝土抗壓強度發(fā)展規(guī)律的研究[J];商品混凝土;2010年09期

7 張建明;徐曉蓮;;堿激發(fā)地聚合物膠凝材料制備技術(shù)的優(yōu)化[J];鄂州大學學報;2010年05期

8 王宙;王晴;丁兆洋;劉磊;;養(yǎng)護制度對礦渣基無機礦物聚合材料力學性能的影響[J];新型建筑材料;2010年08期

9 王晴;張崇燕;丁兆洋;隋智通;;無機礦物聚合物混凝土收縮性能的研究[J];材料導報;2010年10期

10 鄭文忠;陳偉宏;王英;;堿礦渣膠凝材料的耐高溫性能[J];華中科技大學學報(自然科學版);2009年10期

，

本文編號：1638489