本文關(guān)鍵詞： 銀包銅粉 類球狀 超聲波分散 抗氧化性　出處：《熱加工工藝》2017年10期 　論文類型：期刊論文

【摘要】：以類球狀銅粉為基體,在超聲波和機(jī)械攪拌分散條件下,采用液相還原法在銅粉表面沉積鍍銀層制備銀包銅粉。觀察其表觀色澤,測試其松裝密度、粒度分布、比表面積、導(dǎo)電性和抗氧化性。采用SEM/EDS、XRD表征銀包銅粉的形貌、成分和相組成。結(jié)果表明:采用此種方案制備出的銀包銅粉的顏色為銀白色,銀含量45.7%、松裝密度1.62 g/cm~3、粒徑D_(50)為8.290μm、比表面積為0.749 m~2/g,導(dǎo)電性能良好,抗氧化性能較佳,所制備的銀包銅粉具有良好的應(yīng)用前景。
[Abstract]:Silver coated copper powder was prepared on the surface of copper powder by liquid phase reduction under the condition of ultrasonic and mechanical agitation dispersion. The apparent color of silver coated copper powder was observed, and its loose density, particle size distribution and specific surface area were measured. The morphology, composition and phase composition of silver coated copper powder were characterized by SEM / EDS- XRD. The results showed that the color of silver coated copper powder prepared by this method was silver white. The silver content is 45.7%, the density of loose packing is 1.62 g / cm ~ (-3), the diameter of DZ _ (50) is 8.290 渭 m, the specific surface area is 0.749 mm2 / g, the conductivity is good, the oxidation resistance is good, and the silver coated copper powder has good application prospect.
【作者單位】： 昆明理工大學(xué)材料科學(xué)與工程學(xué)院;
【基金】：國家科技型中小企業(yè)創(chuàng)新基金資助項(xiàng)目(14C26215303257) 昆明理工大學(xué)分析測試基金資助項(xiàng)目(20140061)
【分類號】：TB331;TB383.3

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 婁萃;蔡曉蘭;;銀銅粉的研制及性能的研究[J];南方金屬;2006年06期

2 王玉棉;于夢嬌;王勝;侯新剛;趙燕春;;超細(xì)銅粉的制備方法、存在問題及應(yīng)用[J];材料導(dǎo)報(bào);2007年S1期

3 胡敏藝;徐銳;王崇國;周康根;;超細(xì)球形銅粉的制備[J];功能材料;2007年10期

4 蔡報(bào)珍;;超細(xì)銅粉的制備及應(yīng)用[J];江西有色金屬;2008年04期

5 黃凌云;朱國才;池汝安;霍慧彬;;我國超細(xì)銅粉研究及生產(chǎn)現(xiàn)狀[J];化學(xué)通報(bào);2008年05期

6 王文清;;歧化反應(yīng)制備超細(xì)銅粉[J];武漢工業(yè)學(xué)院學(xué)報(bào);2008年02期

7 劉維平;邱定蕃;于月光;;超聲場輔助礦漿電解法制備超細(xì)銅粉[J];中國有色金屬學(xué)報(bào);2008年07期

8 劉維平;;制備細(xì)銅粉的新方法[J];粉末冶金技術(shù);2008年05期

9 王尚軍;方曉祖;余宗寶;;超細(xì)球形銅粉的制備工藝研究[J];中國粉體技術(shù);2009年01期

10 薛麗梅;李雙志;劉，

本文編號：1495949