【摘要】：模擬火災(zāi)現(xiàn)場中銅包鋼導(dǎo)線熔痕產(chǎn)生的條件,制備一、二次短路熔痕和火災(zāi)熱作用導(dǎo)線痕跡。使用金相分析法,尋找最佳金相浸蝕劑,研究一、二次短路熔痕的金相組織特點。結(jié)果表明,4%硝酸酒精是最佳浸蝕劑,一次短路熔痕的組織以較細(xì)的馬氏體為主,及少量暗色托氏體,存在氣孔;二次短路熔痕中以馬氏體為主,晶界處有鐵素體析出,不存在托氏體,幾乎沒有氣孔存在。
[Abstract]:The condition that the copper-clad steel wire of the copper-clad steel wire in the fire field is simulated is simulated, and a lead trace of a secondary short-circuit melting mark and a fire thermal effect is prepared. Metallographic analysis method is used to find the best metallographic etching agent, and the metallographic structure of the secondary short-circuit fusion mark is studied. The results show that 4% of the nitric acid alcohol is the best etching agent, the microstructure of the primary short-circuit melting mark is dominated by the fine martensite, and a small amount of dark troostite exists in the secondary short-circuit melting mark, and the martensite is the main material in the secondary short-circuit melting mark, and the grain boundary is provided with ferrite to separate out, no supporting body exists, and almost no air hole exists.
【作者單位】： 中國人民武裝警察部隊學(xué)院;
【分類號】：TG115.21;D918.91

【相似文獻(xiàn)】

相關(guān)期刊論文 前7條

1 楊學(xué)林;陳亞鵬;蔡莊紅;田克情;;復(fù)合無機(jī)鹽法分離銅包鋼復(fù)合金屬[J];河北省科學(xué)院學(xué)報;2011年04期

2 朱敏;杜翠薇;黃亮;劉智勇;趙天亮;李瓊;李曉剛;;含水量對連鑄銅包鋼在大港土壤中腐蝕行為的影響[J];中國腐蝕與防護(hù)學(xué)報;2014年01期

3 張愷槞;;淺談銅包鋼接地施工工藝及技術(shù)要求[J];中國石油和化工標(biāo)準(zhǔn)與質(zhì)量;2013年03期

4 費(fèi)明冰,陳正宏;銅包鋼芯線生產(chǎn)工藝的研究[J];電鍍與精飾;1998年04期

5 閆愛軍;王玉娜;鄭博野;廖強(qiáng)強(qiáng);;不同pH值的土壤溶液中銅包鋼的腐蝕行為研究[J];全面腐蝕控制;2014年08期

6 朱敏;杜翠薇;李曉剛;劉智勇;王勝榮;李建寬;賈靜煥;;純Cu和銅包鋼在大港土壤環(huán)境中的腐蝕行為研究[J];中國腐蝕與防護(hù)學(xué)報;2013年06期

7 ;[J];;年期

，

本文編號：2501060